Mechanical deformation of elastomer medical devices can enable microbial surface colonization
HomeHome > Blog > Mechanical deformation of elastomer medical devices can enable microbial surface colonization

Mechanical deformation of elastomer medical devices can enable microbial surface colonization

Aug 25, 2023

Scientific Reports volume 13, Article number: 7691 (2023) Cite this article

784 Accesses

39 Altmetric

Metrics details

Elastomers such as silicone are common in medical devices (catheters, prosthetic implants, endoscopes), but they remain prone to microbial colonization and biofilm infections. For the first time, our work shows that rates of microbial surface attachment to polydimethylsiloxane (PDMS) silicone can be significantly affected by mechanical deformation. For a section of bent commercial catheter tubing, bacteria (P. aeruginosa) show a strong preference for the ‘convex’ side compared to the ‘concave’ side, by a factor of 4.2. Further testing of cast PDMS materials in bending only showed a significant difference for samples that were manually wiped (damaged) beforehand (1.75 × 104 and 6.02 × 103 cells/mm2 on the convex and concave sides, respectively). We demonstrate that surface microcracks in elastomers are opened under tensile stress (convex bending) to become ‘activated’ as sites for microbial colonization. This work demonstrates that the high elastic limit of elastomers enables these microcracks to reversibly open and close, as ‘dynamic defects’. Commercial catheters have relatively high surface roughness inherent to manufacturing, but we show that even manual wiping of newly-cast PDMS is sufficient to generate surface microcracks. We consider the implication for medical devices that feature sustained, surgical, or cyclic deformation, in which localized tensile conditions may expose these surface defects to opportunistic microbes. As a result, our work showcases serious potential problems in the widespread usage and development of elastomers in medical devices.

Elastomers such as silicones, polyurethanes and polyvinylchloride (PVC) were first used in medical devices in the 1950s and are now in widespread use. Examples include polydimethylsiloxane (PDMS) urinary catheters, polyurethane PICC catheters, endoscope sheaths, and a wide range of reconstructive plastic surgery products, such as silicone prosthetic breast or facial implants1,2. Recently silicones have been the basis for a new generation of artificial heart and prosthetic heart valves as silicones have low thrombogenicity, good chemical stability and versatile manufacturability3. In addition to implanted devices, elastomers are common in extracorporeal medical devices such as pumps and tubing in dialysis systems.

Despite their widespread use, the microbial colonization of elastomeric devices, and subsequent development to biofilm-based infections, remain a persistent problem both for implanted and reusable devices. Device associated infections are responsible for 50–70% of the nearly 2 million healthcare-associated infections (HAIs) in the US4,5. HAIs significantly increase adverse health risks, length of hospital stays for patients and treatment costs. The majority of device-associated infections are a result of bacterial colonization on catheters, including central-line associated bloodstream infections (CLABSI), catheter-associated urinary tract infections (CAUTI), and ventilator-associated pneumonia (VAP)6,7. Of the more than 5 million central line catheters inserted per year in the US, 3–5% of these patients suffered from CLABSIs, increasing treatment costs significantly8. A recent comparative analysis of patients requiring intravenous catheterization showed infection caused an average of 2 additional days hospital stay9.

Device-associated infections begin with the initial colonization of the surface by microbial pathogens and subsequent development into a biofilm10,11,12. Cells in a biofilm produce extracellular polymeric substances, which protect them from disinfectants, antibiotics and host defense mechanisms and as a result biofilms are persistent and difficult to eradicate5,13,14,15,16,17,18,19. Various gram-positive bacteria (Enterococcus faecalis, Staphylococcus aureus, S. epidermidis), gram-negative bacteria (Escherichia coli, Klebsiella pneumoniae, Proteus mirabilis, Pseudomonas aeruginosa), and fungi (Candida albicans) are commonly isolated from explanted medical devices12. These pathogens are known to develop multidrug resistance and once they form biofilms the use of systemic, broad-spectrum antibiotics is often ineffective. If infected, the removal and replacement of device is often a necessity, which can be a highly traumatic and medically risky option with a high likelihood for re-infection12.

The material factors that determine when and where these bacterial colonies initially attach on devices are not well understood. Certainly, there are known risks (probabilities) of contamination events, such as central venous catheters (CVC) picking up flora from skin during insertion or blood-borne pathogens colonizing implant surfaces (in the ‘race to the surface’)20,21. However, device-associated infection events remain difficult to predict.

Thus, we aim to better understand the initial stages of microbial surface colonization. In this work we uncover an entirely new mechanism for microbial colonization associated with surface defects and the mechanical deformation of elastomer biomaterials.

We begin with a preliminary observation that bending deformation of elastomer devices influences bacterial colonization. Sections of a commercial silicone Foley catheter (Rusch OD 4.7 mm, 5 mL) (Fig. 1a) were cut and exposed to a P. aeruginosa (PAO1) culture within the wells of a standard 6-well plate (Fig. 1b). The catheter sections were either kept straight (unbent), or were cut slightly long, to cause them to bend within the wells (mid-point displacement of 4 mm, and 1.9 cm radius of curvature). The samples (n = 5) were suspended at the mid-point of wells, so that cells had free access to all surfaces. After 4 h (25 °C), the samples were fixed with glutaraldehyde (GDA) and Tween-20 and stained with Sytox green (30 min).

Bending deformation of elastomer devices influences bacterial colonization. (a) Commercial silicone Foley urinary catheter (Rusch, OD 4.7 mm, 5 mL); (b) Culture of P. aeruginosa (25 °C, static culture, LB media) with catheter sections in a straight (unbent) or bent condition; (c) Representative fluorescence microscopy images of P. aeruginosa (Sytox-stained) on the convex and concave outer surfaces of the catheter tubing, after 4 h growth, showing significantly higher growth on the convex side.

In fluorescence imaging (Fig. 1c), the bent sections of catheter tubing showed a significantly higher density of cells on the convex (tensile) side (2.11 ± 0.19 × 104 cells/mm2), compared to the concave (compressive) side (4.94 ± 0.3 × 103 cells/mm2) by a factor of about 4.2. The unbent samples showed a uniform cell density throughout (1.35 ± 0.47 × 104 and 1.39 ± 0.48 × 104 cells/mm2 on sides A and B, respectively).

The question is why are the bacteria 4 times more likely to colonize the convex surface of these bent catheters? A correlation between bacterial surface attachment and mechanical bending has not been reported before. There are many surface factors that affect rates of microbial surface attachment, including material properties (surface chemistry, charge, roughness and hydrophobicity)22,23,24,25 and hydrodynamic shear26. However, in our case, both sides of the tubing have identical material properties. It is also reported that bacteria can sense mechanical stress27. In our case, the cells colonize these tensile or compressed surfaces after the tubing is bent, and therefore the cells themselves do not experience strain. If we consider any effects of structural curvature, we can note the radius of bending (50 mm) is orders of magnitude larger than the cell size, so it is unlikely cells ‘notice’ any local curvature differences.

We suggest the most relevant factor explaining the results of Fig. 1 is the due to changes in local surface roughness (Ra) and topography in elastic bending. Generally it is well-known found that increases in surface roughness at the nano- and microscale cause increased rates of microbial colonization, for a wide range of materials and microbes25,28,29,30,31,32,33,34,35. For example, the adhesion rate of P. aeruginosa on rough (Ra = 0.9 µm) stainless steel surface can be 102 times higher compared to an electropolished (Ra = 0.1 µm) steel36. Previously, we have also shown a ~ 1 log CFU cm−2 reduction in P. aeruginosa on mirror finished (Ra = 0.09 µm) compared to standard roughness (Ra = 0.18 µm) stainless steel37. Many studies have noted a strong preferential attachment and alignment to topographical surface defects such as grooves or scratches for various bacterial strains38,39,40,41,42. While the strong preference for microbial alignment to surface defects is not well understood, it appears that defects increase cell-surface contact area, protect the cells from shear forces, and greatly enhance the binding potential and surface adhesion43,44. Research shows that the initial adhesion sites on rough substrates occurs in pits, cracks, and defect sites45,46. Studies in bacterial-probe AFM have also shown that the retention forces are higher for bacteria attached in defect sites on rougher substrates compared to smooth controls43.

Elastomer catheters and medical devices formed by extrusion and injection molding typically have an average surface roughness (Ra) in the range of 50 to 500 nm47, with surface defects in the form of grooves or striations formed by extruding conditions common47,48,49. Baldassari et al. in 1994 were among the first to point out that surface defects (grooves, scratches) are preferential sites for bacterial colonization of medical devices50. As an example, Buijsssen et al. found that lower silicone roughness reduced both bacterial and yeast fouling rates49.

Here we suggest that even when silicone elastomers do show a low surface roughness (Ra < 0.5 µm), and appear ostensibly smooth to the eye (high surface reflectance), ‘dynamic’ microcracks are present, which are mechanically opened and closed in elastic bending. Specifically, a certain population of microcracks may be opened (exposed), or closed, on the convex (tensile) and concave (compressive) sides of bent elastomers, but otherwise remain effectively hidden from view when undeformed. This mechanism is enabled by the very large reversible, elastic strains that are characteristic of elastomer materials, and their ability to effectively ‘re-seal’ themselves. This mechanism may have significant implications in further understanding device-associated infection for a wide range of elastomer medical devices in widespread use (catheters, heart valves, prostheses). In this work we demonstrate this deformation-associated ‘dynamic’ defect mechanism for PDMS silicone, for both newly-cast (undamaged) and damaged conditions.

We tested the attachment of P. aeruginosa cells on sections of the commercial PDMS catheter (Fig. 1a) and cast PDMS, cured in flat petri dishes (Sylgard 184, Dow Corning). The inherent average roughness (Ra) of the catheter and cast PDMS were found to be 1.78 ± 0.3 and 0.1 ± 0.02 µm, respectively. We exposed the catheter and cast PDMS samples (0.5 × 0.5 × 5 cm (HxWxL)) to mild surface abrasion to induce surface damage, by wiping repeatedly with lab tissue (Kim-Wipe, Kimberly Clark, 50 uni-directional wipes). As a result, samples were categorized as ‘new’ or ‘wiped’. All samples were rinsed with deionized water, sterilized with ethanol (70%), then placed into 6-well plates and bent with a mid-point deflection of 4 mm (corresponding to a strain of 3%), while control samples were cut slightly shorter to remain in a straight, unbent condition (Fig. 1b). P. aeruginosa (PAO1) inoculated into LBNS growth medium (5 mL, 1% PAO1) was then added to each well plate and incubated at room temperature (25 °C).

Figure 2a,b shows average cell counts from fluorescence image analysis (cellSens, Olympus BX63) for the catheter and cast PDMS samples, with images for the cast PDMS in Fig. 2c. The catheter PDMS samples showed significantly higher cell density on the convex side of bending in both the ‘new’ and ‘wiped’ conditions, compared to the unbent samples, or concave side. For the cast PDMS there was no measurable effect of bending on cell density for the new (undamaged) samples. However, for the wiped samples of cast PDMS, the bacterial cells again showed a preference for the convex side; 1.75 × 104 cells/mm2 (convex), and 6.02 × 103 cells/mm2 (concave), a ratio of 2.9. For both catheter and cast PDMS, the wiped samples showed significantly higher cell densities compared to the new (unwiped) samples.

(a,b) Bacterial colonization of catheter and PDMS surfaces. P. aeruginosa (PA01, 25 °C for 4 h) counts by fluorescence image analysis on the unbent, convex and concave surfaces of catheter tubing and cast PDMS, for both ‘new’ and ‘wiped’ samples showing statistically higher attachment on tensile surfaces of damaged silicone (wiped) but not on ‘new’ samples; (c) BF and fluorescence imaging of the new and wiped cast PDMS surfaces for the unbent, convex and concave samples. Wiping induced microcracking on the surface, which lead to increased bacterial attachment; (d) Schematic of deformation-induced opening of dynamic surface microcracks that enable bacterial colonization. These are opened and exposed in tensile bending, but remain effectively hidden (closed) in unbent and compressed states.

The results of Fig. 2 highlight that the new cast PDMS is ‘immune’ to this effect of tensile deformation in increasing rates of bacterial surface colonization, and that some degree of surface damage is required for this effect to occur. In this case, the surface wiping was enough to generate defects, in the form of microscale scratches, grooves or cracks (as seen in the brightfield images of Fig. 2c). We propose that a population of these surface microcracks, at the scale of microbial cells, are only exposed and ‘visible’ to cells upon tensile deformation (Fig. 2d). Compression of the samples (concave side) appears to generally close these microcracks and make them effectively invisible to the bacteria as attachment sites. Interestingly, the commercial catheter PDMS has sufficient surface roughness, due to extrusion manufacturing, to cause this deformation-induced colonization for both the new and wiped samples (Figs. 1, 2). The newly cast PDMS has very low surface roughness, but basic handling and cleaning procedures (such as wiping), were enough to induce sufficient surface damage to enable the effect of deformation-induced crack opening.

To assess the effect of wiping to elastomer devices, we analyzed the surface topography and measured the average roughness (Ra) with optical profilometry (Contour GT-3D, Bruker). 3D surface profiles of the cast PDMS (Fig. 3a) showed surface wiping increases surface damage compared to new PDMS. Further, the surface defects generally did effectively ‘disappear’ in compression (concave bending), while increased in both width and depth in tension (convex). The average roughness (Ra) of the wiped PDMS decreased from 0.75 ± 0.04 μm (unbent) to 0.20 ± 0.02 μm in compression and increased to 1.1 ± 0.1 μm in tension (Fig. 3c). The depth of the ‘opened cracks’ (Fig. 3b) is closely matched to typical bacterial cell sizes, such as P. aeruginosa (0.5 μm wide and 2–3 μm long) as seen in the 2D surface profiles for the wiped PDMS (Fig. 3b) where the depth reached values of 3 μm at an average width of 5 μm. After an overnight culture (12 h) of P. aeruginosa on newly cast and wiped PDMS, there was a log increase in cell density of 1–1.5 on the wiped sample compared to the smooth control (Fig. 3d,e). The work of Kargar et al. is consistent with these results, which showed a significant increase in cell density if the spacing of defects are wider than the cell width51.This further indicates the role of surface topographical defects in providing preferential attachment sites, leading to increased cellular density and biofilm development. The effect of wiping cycles on cast PDMS are further explored in Supplemental Fig. S1. By wiping the surface of cast PDMS between 1 to 100 times, the roughness of cast PDMS increased from a value of 0.1 to 1.25 μm, respectively. Concurrently, increasing wiping cycles showed an increase in the overall attachment of PAO1 to PDMS (2 h incubation of 1% PAO1 in LBNS), highlighting the sensitivity of elastomer materials to surface damage, even when generated through short term wiping contact with a tissue.

Surface topography and bacterial attachment of new and wiped PDMS exposed to bending. (a) Three-dimensional (3D) optical profilometer images showing the surface topography for the unbent, convex and concave samples of new (top row) and wiped (bottom row) sections of cast PDMS; (b) Representative surface profiles for ‘wiped’ PDMS; (c) Average roughness, Ra, for wiped PDMS; (d) Fluorescence microscopy imaging and (e) associated cell counts (CFU/cm2) for the new and wiped PDMS surfaces (scale bar = 25 μm).

Generally, microscale surface defects have not been well-studied or characterized for elastomer biomaterials, and this transient nature of defects and their dependence on dynamic mechanical deformations has never been reported before. Studies aimed at understanding device infections, have noted bacterial colonization on explanted elastomer devices such as catheters and endoscopes on and around surface defects, although these defects are not analyzed in terms of depth or size50,52,53,54,55,56. Most relevant to this work is that of Santos et al. who induced damage to endoscope working channels through sequential forcep passes and concluded that this damage increased bacterial colonization due to an increased average roughness (Ra)56. Both the size-dependence of damaged regions and the susceptibility of tensile regions of deformed medical devices to microbial colonization have not been identified before.

To further test the susceptibility of elastomers to surface damage, we tested the generation of patterned surface cracks in PDMS using systematic, controlled compressive force (EVG 520 semi-automated Hot Embosser). A patterned polystyrene sheet of a ‘saw-tooth’ groove topography (FLEXcon, USA; 30 µm pitch) was pressed against cast PDMS (Fig. 4a). At sufficient force (17 kN over a 5cm2 area), optical profilometry imaging (Fig. 4b) of the ‘embossed’ PDMS shows a clear pattern of parallel microcracks, with a maximum depth of 5.5 μm and average depth of 1.4 μm. It is interesting to note that after embossing, the PDMS still macroscopically appears as undamaged (high light reflectance, Fig. 4a). When cultured with P. aeruginosa (PAO1) (2 h, 25 °C), the cells showed a very clear preferential attachment to these parallel microcrack defect sites (Fig. 4c). SEM imaging (Fig. 4d) of the PDMS also highlighted the strikingly high degree of alignment of the cells with these patterned surface microcracks. Many cells also appear to be partially trapped within these re-sealed cracks.

(a) Generation of patterned microcracks by ‘press embossing’ a saw-tooth topography (30 µm pitch) against new cast PDMS. The embossed sample appears undamaged to the eye (light reflectance). (b) Two-dimensional (2D) Optical profilometry image of the saw-tooth pattern embossed PDMS showing parallel patterned microcracks roughly 4–5 μm deep. (c,d) Fluorescence and SEM images of P. aeruginosa (PA01) attachment on the embossed PDMS samples, showing highly preferential attachment along the patterned microcracks, after 2 h culture (25 °C).

Our work raises two unexpected issues about the microbial colonization of elastomer biomaterials. One is that elastomers such as silicones can develop surface damage, in the form of microscale scratches and grooves, through even relatively mild contact such as wiping or localized surface compression, which act as preferential attachment sites for microbes. The second, most importantly, is that some significant population of these defects are reversibly opened and closed through bending deformations, making them ‘dynamic’ as they only become available, and active, under local tensile conditions.

Clinically, this work raises questions about surgical handling procedures for elastomer medical devices, such as wiping, pinching and bending, that may occur in surgery or disinfection (endoscopes), which may be introducing surface microcrack defects. Our work shows that wiping or pressing can introduce highly localized tensile stress states, and enough to cause local fracture or tearing events. The manufacturing of commercial devices itself does appear to already generate such surface defects (as shown in our results for a commercial catheter). The standards for the surface roughness and defect population of medical devices are not well defined. Catheters are subject to approval and acceptance under ISO regulation (ISO 10993, for example), in which the only requirement is that defects cannot be visible to the naked eye or through 2.5 × magnification, whereby micro-scale defects can be easily missed57,58.

Surface grooves and microcracks strongly attract initial bacterial attachment (as demonstrated in Fig. 4c), as the first stage of biofilm colony development and device-associated infection, as they provide a protected environment from shear. Surface defects increase the binding affinity through an increase in retention and attachment forces of cells to surfaces43,45. There is also evidence that this attachment can be influenced by extracellular appendages (flagella and pilli) to help anchor the planktonic cell59,60,61. In general, patterned regions of the same height or shorter than the length of a flagellum are susceptible to this anchoring, which can be between 5 to 20 μm34,62. In this case, the flagellum of the species (a singular polar flagellum for PAO1 of about 5 μm63) could easily access the damaged regions, which were about 5 μm wide and 3–5 μm deep. When anchored into these defect sites, the further restriction to flagellar rotation and movement can produce a mechanical signal, which may constitute another example of bacterial mechanosensing.

Our work suggests these dynamic defects may remain effectively hidden or invisible (literally, Fig. 4a) for a device in an undeformed state, but become opened under tension, to enable microbial colonization. Thus, areas of tensile deformation become preferential sites for biofilm initiation. This mechanism of deformation-controlled, dynamic surface defects enabling the initiation of microbial colonization has not been reported before. It appears that these microcracks are able to re-seal again, when relaxed. The mechanism of reversible opening and closing of microcracks is due to the particular mechanical properties of elastomers to allow extremely high, reversible strains without failure; examples include polyurethane (50–100%) and silicones (100–160%)64,65. By comparison, the typical maximum strain (elastic limit) for thermoplastics or metals is significantly less; for example, high density polyethylene (HDPE) is just 3%, Ti alloys 1.2–1.5%, and 316L stainless steel 0.1–0.3%. As plastic deformation is initiated beyond the elastic limit, surface cracks cannot open and close reversibly, as they would for elastomers.

We suggest that a wide range of elastomer medical devices may be susceptible to microbial colonization in areas of tensile deformation, beyond just catheter tubing. For example, opened microcracks may effectively ‘carry’ microbes into the body during surgical insertion, protect microbes from disinfection, or provide temporary active sites for opportunistic colonization in cyclic deformation.

We have considered how medical device deformation may be classified in terms of mechanical deformation, and included examples in each category (Fig. 5). These are devices with; (i) sustained deformation (the device remains deformed while in use); (ii) surgical deformation (the device is deformed during surgical insertion); and (iii) cyclic deformation (periodic deformation). Many devices may experience combinations of these effects.

Implanted devices that feature sustained deformation; such as CVC catheter, in bending,7,20,21, and urinary catheters (balloon inflation)69,70. Medical devices that feature deformation during surgical implantation, such as prosthetic silicone breast implants71,72, endoscopes and bronchoscopes55,73,74. Other examples include contact lenses, facial implants75,76,77,78. Finally, devices which feature cyclic deformations, in particular, which can include tricuspid prosthetic heart valves79,80,81, extracorporeal peristaltic pumps (dialysis or ECMO), and prosthetic finger joints82,83,84,85,86.

Examples of sustained deformation include devices such as catheters, shunt or cannula tubing, which are deformed in surgical insertion and remain bent while in use. For example, the deformation of a CVC catheter can exceed 90° to access the central venous bloodstream (and remain in place for weeks), generating local tensile stress. Another example are Foley urinary catheters which feature an expanded balloon (to physically hold in place), and thereby generating significant biaxial tensile stress across the balloon surface. These tensile regions may have a higher probability of biofilm formation, as a result.

Surgically deformed devices can include catheters, tracheostomy tubes, diagnostic devices such as endoscopes or bronchoscopes, and implanted devices such as prosthetic breast implants. Surgical deformation could potentially open microcracks while exposed to skin microflora and contaminated hands, carrying these pathogens into the body. Endoscopes often feature elastomer sheaths, and experience high strains (degree of curvature) within the very high microbial dense areas of the gastrointestinal tract. As discussed below, infectious disease transmission is not uncommon, despite standard disinfection. We suggest areas of tensile deformation, trapping bacteria, may be the reason. Certain implanted devices, such as silicone breast implants, experience high deformations during minimally invasive surgery, achieved by compressing the implants into curved incisions placed around the areola66,67. Through the manual and tool mediated compression of these implants to half their initial diameter, large local stresses and abrasive damage can be sustained by the implant66. There have been significant clinical problems and controversy associated with silicone breast implants (inflammation, contraction and failure), particularly in the 1990s (resulting in a temporary FDA ban), which was attributed partially to bacterial infection68. The root causes could not be traced to the material alone, leading to their re-approval. Based on our experimental results, we speculate that the generation and opening surface microcracks during surgical insertion, contaminated with skin microflora, may have been (and continue to be) a contributing factor to infection complications.

Cyclic deformations occur in devices such as prosthetic heart valves. As an example of biological elastomers, bovine and porcine tissue prosthetic heart valves sustain large strains in use. While native human tissues exhibit a strain at failure of 18–29%, porcine and bovine valves sustain 48–70% and 87–120% strain at failure, respectively87. We suggest that this newly-recognized mechanism for deformation-associated microbial colonization may be a contributing factor for Prosthetic valve endocarditis (PVE). Finally, cyclic deformation of elastomers can also occur in extracorporeal devices, such as peristaltic pumps with dialysis or ECMO systems, in the local compression of silicone tubing.

An additional concern is for medical devices which are reused or repurposed such as endoscopes, duodenoscopes and bronchoscopes. Infectious disease transmission between patients remains a concern, despite standard disinfection protocols, for multidrug-resistant bacterial strains of K. pneumonia, E. coli, and Enterococci73,74,88,89,90,91. Similarly, endoscopes which are also reprocessed through cleaning steps which include manual wiping, have been shown to become damaged (surface cracks, scratches) and can remain contaminated53,55,56,92. Endoscope disinfection often involves coiling the device, putting the inner radii surfaces in compression. While speculative, we hypothesize microbes may be trapped within these closed, re-sealed microcrack environments, and potentially protected from disinfection as a result.

Elastomers and thermoplastic materials are excellent candidates for medical devices from a mechanical and chemical standpoint, as evidenced by their increased prevalence in medical device design. However, device-associated infection remains a persistent problem in healthcare. Our work shows that, ironically, the very high elastic strain limit of these materials may also be contributing to this mechanism for microbial colonization. Our work seeks to define new classifications of medical device deformations for the first time. Each type of deformation may enable these sites of surface damage to be ‘activated’ to increase susceptibility for infection. This work may give us more understanding how and where such infections occur, clinically.

PDMS resin and crosslinker (Dow Sylgard 184) were mixed at a weight ratio of 10:1. PDMS was degassed under vacuum (VWR vacuum oven) at room temperature for 30 min. 25 g of the PDMS was poured into a 100 mm petri dish (VWR) and cured at 60 °C for 24 h. PDMS strips were cut to either 34.8 mm long by 6 mm wide (unbent) or 36.3 mm long by 6 mm wide (bent) to fit into a standard 6 well plate (VWR). Elastomer surface abrasion was done by wiping 50X full 360° rotations with a Kim-wipe tissue in direction parallel to the axis of bending. The patterned surface cracks were generated by ‘press embossing’ (EVG 520 semi-automated Hot Embosser) a saw-tooth topography (30 µm pitch) against newly cast PDMS. All PDMS samples were cleaned by rinsing in DI water and ethanol sequentially, 5X.

Standard conditions were followed to prepare bacterial cultures. A preculture of Pseudomonas aeruginosa PAO1 was prepared by obtaining a single colony from an overnight cultured lysogenic agar media plate incubated at 37 °C overnight. This colony was inoculated into 5 mL of LB and incubated overnight at 37 °C under constant agitation. The bacterial suspension was prepared by adding 1% of the preculture to LB broth with no salt. 10 mL of the bacterial suspension was pipetted into the 6-well plates with the PDMS samples, and incubated for 4 h at 25 °C in static culture. The PDMS samples were rinsed afterwards in 10 mL of 1X PBS buffer three times, and then submerged in a 1% GDA (Sigma Aldrich) saline solution (10 mL) for 20 min. After fixing, the PDMS sections were submerged in a 0.05% Tween-20 (Sigma Aldrich) in saline for 20 min and stained for 30 min using a 50 μL Sytox Green (Life Technologies) in 1X PBS buffer pipetted over each contaminated side of the PDMS. The PDMS was imaged by fluorescence microscopy (Olympus BX63, Japan) using 20X and 50X air objectives, and a GPF filter (λex/λem 395/470 nm). Image analysis, image filtering, and cell counts were performed with the Olympus cellSens imaging software.

Surface roughness and topography maps were obtained using a non-contact three dimensional Optical profilometer (Bruker Contour GT-K, Tucson, AZ, USA). After calibrating the system scanner, the sample was placed on the microscope stage and the camera was adjusted to focus on the surface microstructure by raising or lowering the z-axis until the appearance then disappearance of two sets of fringes. Measurement was then performed using the vertical scanning interferometry (VSI) mode and focused to determine its upper and lower and upper images using a 20X objective. Results are displayed as 2D contour plot with the X and Y direction cross section plots. Further analysis, using the Bruker Vision 64 Map Premium software, was performed to correct sample tilting and extract surface roughness parameters together with 2D and 3D surface profiles.

All data will be made available by the authors upon request, please contact D. van den Berg ([email protected]).

Johnson, J. R., Kuskowski, M. A. & Wilt, T. J. Systematic review: antimicrobial urinary catheters to prevent catheter-associated urinary tract infection in hospitalized patients. Ann. Intern. Med. 144(2), 116–126 (2006).

Article PubMed Google Scholar

Singha, P., Locklin, J. & Handa, H. A review of the recent advances in antimicrobial coatings for urinary catheters. Acta Biomater. 50, 20–40 (2017).

Article CAS PubMed Google Scholar

Jenney, C. et al. Assessment of a siloxane poly(urethane-urea) elastomer designed for implantable heart valve leaflets. Adv. NanoBiomed Res. 1(2), 2000032 (2021).

Article CAS Google Scholar

Bryers, J. D. Medical biofilms. Biotechnol. Bioeng. 100(1), 1–18 (2008).

Article CAS PubMed PubMed Central Google Scholar

Costerton, J., Stewart, P. S. & Greenberg, E. Bacterial biofilms: a common cause of persistent infections. Science 284(5418), 1318–1322 (1999).

Article ADS CAS PubMed Google Scholar

Richards, M. J., Edwards, J. R., Culver, D. H. & Gaynes, R. P. Nosocomial infections in medical intensive care units in the United States National Nosocomial Infections Surveillance System. Crit. Care Med. 27(5), 887–892 (1999).

Article CAS PubMed Google Scholar

Ryder, M. A. Catheter-related infections: It's all about biofilm. Top. Adv. Pract. Nurs. eJournal 5(3), 2005 (2005).

Google Scholar

Scott, R. D. The Direct Medical Costs of Healthcare-Associated Infections in US Hospitals and the Benefits of Prevention (2009).

Lim, S. et al. Increased clinical and economic burden associated with peripheral intravenous catheter-related complications: analysis of a US hospital discharge database. Inquiry 56, 0046958019875562 (2019).

PubMed PubMed Central Google Scholar

Mittelman, M. W. [39] Recovery and characterization of biofilm bacteria associated with medical devices. Methods Enzymol. 310, 535–551 (1999).

Article Google Scholar

Elder, M. J., Stapleton, F., Evans, E. & Dart, J. K. Biofilm-related infections in ophthalmology. Eye 9(1), 102–109 (1995).

Article PubMed Google Scholar

Donlan, R. M. Biofilms and device-associated infections. Emerg. Infect. Dis. 7(2), 277 (2001).

Article CAS PubMed PubMed Central Google Scholar

Hall-Stoodley, L., Costerton, J. W. & Stoodley, P. Bacterial biofilms: from the natural environment to infectious diseases. Nat. Rev. Microbiol. 2(2), 95–108 (2004).

Article CAS PubMed Google Scholar

Reid, G. Biofilms in infectious disease and on medical devices. Int. J. Antimicrob. Agents 11(3), 223–226 (1999).

Article CAS PubMed Google Scholar

Loo, C.-Y. et al. Implications and emerging control strategies for ventilator-associated infections. Expert Rev. Anti Infect. Ther. 13, 379–393 (2015).

Article CAS PubMed Google Scholar

Campoccia, D., Montanaro, L. & Arciola, C. R. A review of the biomaterials technologies for infection-resistant surfaces. Biomaterials 34(34), 8533–8554 (2013).

Article CAS PubMed Google Scholar

Bjarnsholt, T., Ciofu, O., Molin, S., Givskov, M. & Høiby, N. Applying insights from biofilm biology to drug development [mdash] can a new approach be developed?. Nat. Rev. Drug Discov. 12(10), 791–808 (2013).

Article CAS PubMed Google Scholar

Høiby, N., Bjarnsholt, T., Givskov, M., Molin, S. & Ciofu, O. Antibiotic resistance of bacterial biofilms. Int. J. Antimicrob. Agents 35(4), 322–332 (2010).

Article PubMed Google Scholar

Davies, D. Understanding biofilm resistance to antibacterial agents. Nat. Rev. Drug Discov. 2(2), 114–122 (2003).

Article MathSciNet CAS PubMed Google Scholar

Tang, H. J. et al. The impact of central line insertion bundle on central line-associated bloodstream infection. BMC Infect. Dis. 14, 356 (2014).

Article PubMed PubMed Central Google Scholar

Blot, K., Bergs, J., Vogelaers, D., Blot, S. & Vandijck, D. Prevention of central line-associated bloodstream infections through quality improvement interventions: A systematic review and meta-analysis. Clin. Infect. Dis. 59(1), 96–105 (2014).

Article PubMed PubMed Central Google Scholar

O’Grady, N. P. et al. Guidelines for the prevention of intravascular catheter-related infections. Clin. Infect. Dis. 52(9), e162–e193 (2011).

Article PubMed PubMed Central Google Scholar

Tuson, H. H. & Weibel, D. B. Bacteria-surface interactions. Soft Matter 9(18), 4368–4380 (2013).

Article ADS CAS PubMed PubMed Central Google Scholar

Cheng, Y., Feng, G. & Moraru, C. I. Micro- and nanotopography sensitive bacterial attachment mechanisms: A review. Front. Microbiol. 10, 191 (2019).

Article PubMed PubMed Central Google Scholar

Zheng, S. et al. Implication of surface properties, bacterial motility, and hydrodynamic conditions on bacterial surface sensing and their initial adhesion. Front. Bioeng. Biotechnol. 9, 643722 (2021).

Article PubMed PubMed Central Google Scholar

Donlan, R. M. Biofilms: microbial life on surfaces. Emerg. Infect. Dis 8(9), 881–890 (2002).

Article PubMed PubMed Central Google Scholar

Gordon, V. D. & Wang, L. Bacterial mechanosensing: the force will be with you, always. J. Cell Sci. 132(7), jcs227694 (2019).

Article CAS PubMed PubMed Central Google Scholar

Bohinc, K. et al. Available surface dictates microbial adhesion capacity. Int. J. Adhes. Adhes. 50, 265–272 (2014).

Article CAS Google Scholar

Cheng, Y., Feng, G. & Moraru, C. I. Micro-and nanotopography sensitive bacterial attachment mechanisms: A review. Front. Microbiol. 10, 191 (2019).

Article PubMed PubMed Central Google Scholar

Scheuerman, T. R., Camper, A. K. & Hamilton, M. A. Effects of substratum topography on bacterial adhesion. J. Colloid Interface Sci. 208(1), 23–33 (1998).

Article ADS CAS PubMed Google Scholar

Merritt, K., Shafer, J. W. & Brown, S. A. Implant site infection rates with porous and dense materials. J. Biomed. Mater. Res. 13(1), 101–108 (1979).

Article CAS PubMed Google Scholar

An, Y. H. et al. Rapid quantification of staphylococci adhered to titanium surfaces using image analyzed epifluorescence microscopy. J. Microbiol. Methods 24(1), 29–40 (1995).

Article Google Scholar

Truong, V. K. et al. The influence of nano-scale surface roughness on bacterial adhesion to ultrafine-grained titanium. Biomaterials 31(13), 3674–3683 (2010).

Article CAS PubMed Google Scholar

Wu, S., Zhang, B., Liu, Y., Suo, X. & Li, H. Influence of surface topography on bacterial adhesion: A review (Review). Biointerphases 13(6), 060801 (2018).

Article CAS PubMed Google Scholar

Arnold, J. & Bailey, G. Surface finishes on stainless steel reduce bacterial attachment and early biofilm formation: Scanning electron and atomic force microscopy study. Poult. Sci. 79(12), 1839–1845 (2000).

Article CAS PubMed Google Scholar

Vanhaecke, E. et al. Kinetics of Pseudomonas aeruginosa adhesion to 304 and 316-L stainless steel: Role of cell surface hydrophobicity. Appl. Environ. Microbiol. 56(3), 788–795 (1990).

Article ADS CAS PubMed PubMed Central Google Scholar

Awad, T., Asker, D. & Hatton, B. D. Modification of stainless steel food processing surfaces to reduce bacterial biofilm growth. ACS Appl. Mater. Interfaces 10(27), 22902–22912 (2018).

Article CAS PubMed Google Scholar

Edwards, K. J. & Rutenberg, A. D. Microbial response to surface microtopography: The role of metabolism in localized mineral dissolution. Chem. Geol. 180(1–4), 19–32 (2001).

Article ADS CAS Google Scholar

Hochbaum, A. I. & Aizenberg, J. Bacteria pattern spontaneously on periodic nanostructure arrays. Nano Lett. 10(9), 3717–3721 (2010).

Article ADS CAS PubMed Google Scholar

Geesey, G. G. et al. The influence of surface features on bacterial colonization and subsequent substratum chemical changes of 316L stainless steel. Corros. Sci. 38(1), 73–95 (1996).

Article CAS Google Scholar

Medilanski, E., Kaufmann, K., Wick, L. Y., Wanner, O. & Harms, H. Influence of the surface topography of stainless steel on bacterial adhesion. Biofouling 18(3), 193–203 (2002).

Article Google Scholar

Lorenzetti, M. et al. The influence of surface modification on bacterial adhesion to titanium-based substrates. ACS Appl. Mater. Interfaces 7(3), 1644–1651 (2015).

Article CAS PubMed Google Scholar

Wang, C. et al. Effect of enamel morphology on nanoscale adhesion forces of streptococcal bacteria: An AFM study. Scanning 37(5), 313–321 (2015).

Article CAS PubMed Google Scholar

Busscher, H. J. & van der Mei, H. C. How do bacteria know they are on a surface and regulate their response to an adhering state?. PLoS Pathog. 8(1), e1002440 (2012).

Article CAS PubMed PubMed Central Google Scholar

Bollen, C. M., Lambrechts, P. & Quirynen, M. Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention: A review of the literature. Dent. Mater. 13(4), 258–269 (1997).

Article CAS PubMed Google Scholar

Barkarmo, S. et al. Biofilm formation on polyetheretherketone and titanium surfaces. Clin. Exp. Dent. Res. 5(4), 427–437 (2019).

Article PubMed PubMed Central Google Scholar

Bovas, B. C., Karunamoorthy, L. & Chuan, F. B. Effect of extrusion process melt temperature on polyurethane catheter surfaces. Mater. Manuf. Processes 33(2), 180–185 (2018).

Article CAS Google Scholar

Lawrence, E. L. & Turner, I. G. Characterisation of the internal and external surfaces of four types of Foley catheter using SEM and profilometry. J. Mater. Sci. 17(12), 1421–31 (2006).

CAS Google Scholar

Buijssen, K. et al. Influence of surface roughness on silicone rubber voice prostheses on in vitro biofilm formation and clinical lifetime in laryngectomised patients. Clin. Otolaryngol. 42(6), 1235–1240 (2017).

Article CAS PubMed Google Scholar

Baldassarri, L. et al. Microbial colonization of implanted silicone and polyurethane catheters. J. Mater. Sci. Mater. Med. 5(9–10), 601–605 (1994).

Article CAS Google Scholar

Kargar, M., Wang, J., Nain, A. S. & Behkam, B. Controlling bacterial adhesion to surfaces using topographical cues: A study of the interaction of Pseudomonas aeruginosa with nanofiber-textured surfaces. Soft Matter 8(40), 10254–10259 (2012).

Article ADS CAS Google Scholar

Canada, P. H. A. O., Infection prevention and control guideline for flexible gastrointestinal endoscopy and flexible bronchoscopy. Her Majesty the Queen in Right of Canada (2010).

Nelson, D. B. et al. Multi-society guideline for reprocessing flexible gastrointestinal endoscopes. Infect. Control Hosp. Epidemiol. 24(7), 532–532 (2003).

Article PubMed Google Scholar

Tang, J. et al. Highly stretchable electrodes on wrinkled polydimethylsiloxane substrates. Sci. Rep. 5(1), 16527 (2015).

Article ADS CAS PubMed PubMed Central Google Scholar

Ofstead, C. L. et al. Assessing residual contamination and damage inside flexible endoscopes over time. Am. J. Infect. Control 44(12), 1675–1677 (2016).

Article PubMed Google Scholar

Santos, L. C. S. et al. Contribution of usage to endoscope working channel damage and bacterial contamination. J. Hosp. Infect. 105(2), 176–182 (2020).

Article CAS PubMed Google Scholar

ISO, ISO 20696:2018(E). In Sterile Urethral Catheters for Single Use (International Organization for Standardization, 2018).

ISO, ISO 10555-1:2013(E). In Intravascular Catheters—Sterile and Single-Use Catheters—Part 1: General requirements (International Organization for Standardization, 2014).

Friedlander, R. S. et al. Bacterial flagella explore microscale hummocks and hollows to increase adhesion. Proc. Natl. Acad. Sci. USA 110(14), 5624 (2013).

Article ADS CAS PubMed PubMed Central Google Scholar

Friedlander, R. S., Vogel, N. & Aizenberg, J. Role of flagella in adhesion of Escherichia coli to abiotic surfaces. Langmuir 31(22), 6137–6144 (2015).

Article CAS PubMed Google Scholar

Wang, L., Chen, W. & Terentjev, E. Effect of micro-patterning on bacterial adhesion on polyethylene terephthalate surface. J. Biomater. Appl. 29(10), 1351–1362 (2015).

Article CAS PubMed Google Scholar

Bouteiller, M. et al. Pseudomonas flagella: Generalities and specificities. Int. J. Mol. Sci. 22(7), 3337 (2021).

Article CAS PubMed PubMed Central Google Scholar

Hook, A. L. et al. Simultaneous tracking of Pseudomonas aeruginosa motility in liquid and at the solid-liquid interface reveals differential roles for the flagellar stators. MSystems 4(5), e00390-e419 (2019).

Article CAS PubMed PubMed Central Google Scholar

Kim, T. K., Kim, J. K. & Jeong, O. C. Measurement of nonlinear mechanical properties of PDMS elastomer. Microelectron. Eng. 88(8), 1982–1985 (2011).

Article CAS Google Scholar

Stanko, M., Lehmenkühler, P. & Stommel, M. Determination of strain limits for dimensioning polyurethane components. Polymers 13(18), 3198 (2021).

Article CAS PubMed PubMed Central Google Scholar

Fisher, J. Breast augmentation using silicone gel-filled implants. Aesthetic Surg. J. 27(5), 551–557 (2007).

Article CAS Google Scholar

Spear, S. L. & Willey, S. C. Surgery of the Breast: Principles and Art 3rd edn. (Wolters Kluwer/Lippincott Williams & Wilkins, 2011).

Google Scholar

di Pompeo, F. S., Paolini, G., Firmani, G. & Sorotos, M. History of breast implants: Back to the future. JPRAS Open 32, 166–177 (2022).

Article Google Scholar

Cortese, Y. J., Wagner, V. E., Tierney, M., Devine, D. & Fogarty, A. Review of catheter-associated urinary tract infections and in vitro urinary tract models. J. Healthc. Eng. 2018, 2986742 (2018).

Article PubMed PubMed Central Google Scholar

Leuck, A. M. et al. Complications of Foley catheters–is infection the greatest risk?. J. Urol. 187(5), 1662–1666 (2012).

Article PubMed Google Scholar

Pittet, B., Montandon, D. & Pittet, D. Infection in breast implants. Lancet Infect Dis 5(2), 94–106 (2005).

Article PubMed Google Scholar

Basile, A. R., Basile, F. & Basile, A. V. D. Late infection following breast augmentation with textured silicone gel: Filled implants. Aesthetic Surg. J. 25(3), 249–254 (2005).

Article CAS Google Scholar

Larsen, S. et al. Rate and impact of duodenoscope contamination: A systematic review and meta-analysis. eClinicalMedicine 25, 100451 (2020).

Article PubMed PubMed Central Google Scholar

Heuvelmans, M., Wunderink, H. F., van der Mei, H. C. & Monkelbaan, J. F. A narrative review on current duodenoscope reprocessing techniques and novel developments. Antimicrob. Resist. Infect. Control 10(1), 171 (2021).

Article PubMed PubMed Central Google Scholar

Szczotka-Flynn, L. B., Bajaksouzian, S., Jacobs, M. R. & Rimm, A. Risk factors for contact lens bacterial contamination during continuous wear. Optom. Vis. Sci. 86(11), 1216–1226 (2009).

Article PubMed PubMed Central Google Scholar

Thakur, D. V. & Gaikwad, U. N. Microbial contamination of soft contact lenses & accessories in asymptomatic contact lens users. Indian J. Med. Res. 140(2), 307–309 (2014).

PubMed PubMed Central Google Scholar

Patel, K. & Brandstetter, K. Solid implants in facial plastic surgery: Potential complications and how to prevent them. Facial Plast. Surg. 32(5), 520–531 (2016).

Article CAS PubMed Google Scholar

Hasson, O., Levi, G. & Conley, R. Late infections associated with alloplastic facial implants. J. Oral Maxillofac. Surg. 65(2), 321–323 (2007).

Article PubMed Google Scholar

Lalani, T. et al. In-hospital and 1-year mortality in patients undergoing early surgery for prosthetic valve endocarditis. JAMA Intern. Med. 173(16), 1495–1504 (2013).

Article PubMed Google Scholar

Glaser, N., Jackson, V., Holzmann, M. J., Franco-Cereceda, A. & Sartipy, U. Prosthetic valve endocarditis after surgical aortic valve replacement. Circulation 136(3), 329–331 (2017).

Article PubMed Google Scholar

Piper, C., Körfer, R. & Horstkotte, D. Prosthetic valve endocarditis. Heart 85(5), 590 (2001).

CAS PubMed PubMed Central Google Scholar

Nishina, M. et al. A 10-year retrospective cohort study on the risk factors for peritoneal dialysis-related peritonitis: A single-center study at Tokai University Hospital. Clin. Exp. Nephrol. 18(4), 649–654 (2014).

Article PubMed Google Scholar

Ledebo, I. Purification of dialysis fluid: Historical background and perspective. Blood Purif. 27(Suppl 1), 17–19 (2009).

Article PubMed Google Scholar

Tagaya, M. et al. An easy disinfection strategy for pipes connecting hemodialysis equipment. Int. J. Artif. Organs 44(6), 385–392 (2020).

Article PubMed Google Scholar

Majeed, H. Silastic replacement of the first metatarsophalangeal joint: historical evolution, modern concepts and a systematic review of the literature. EFORT Open Rev. 4(3), 77–84 (2019).

Article PubMed PubMed Central Google Scholar

Felländer-Tsai, L., Reinholt, F. P. & Turan, I. Complications with infection and foreign body reaction after silicon implant arthroplasty in the second metatarsophalangeal joint in an adolescent: A case report. J. Foot Ankle Surg. 36(6), 452–456 (1997).

Article PubMed Google Scholar

Soares, J. S. et al. Biomechanical behavior of bioprosthetic heart valve heterograft tissues: Characterization, simulation, and performance. Cardiovasc. Eng. Technol. 7(4), 309–351 (2016).

Article PubMed PubMed Central Google Scholar

Ross, A. S., Baliga, C., Verma, P., Duchin, J. & Gluck, M. A quarantine process for the resolution of duodenoscope-associated transmission of multidrug-resistant Escherichia coli. Gastrointest. Endosc. 82(3), 477–483 (2015).

Article PubMed Google Scholar

Verfaillie, C. J. et al. Withdrawal of a novel-design duodenoscope ends outbreak of a VIM-2-producing Pseudomonas aeruginosa. Endoscopy 47(06), 493–502 (2015).

Article PubMed Google Scholar

Epstein, L. et al. New Delhi metallo-β-lactamase–producing carbapenem-resistant Escherichia coli associated with exposure to duodenoscopes. JAMA 312(14), 1447–1455 (2014).

Article PubMed Google Scholar

Wendorf, K. A. et al. Endoscopic retrograde cholangiopancreatography–associated AmpC Escherichia coli outbreak. Infect. Control Hosp. Epidemiol. 36(6), 634–642 (2015).

Article PubMed Google Scholar

Hailey, D., Jacobs, P. D., Ries, N. M. & Polisena, J. Reuse of single use medical devices in Canada: Clinical and economic outcomes, legal and ethical issues, and current hospital practice. Int. J. Technol. Assess. Health Care 24(4), 430 (2008).

Article PubMed Google Scholar

Download references

We acknowledge the help of Dr. Lindsey Fiddes for critical point drying and SEM imaging, and the help of the Centre for Research and Applications in Fluidic Technologies (CRAFT) at the University of Toronto.

Canadian Foundation for Innovation (CFI) #31799 (BDH), Percy Edward Hart Professorship, University of Toronto (BDH), New Frontiers in Research Fund (NFRF) (BDH), and the Connaught Foundation (BDH).

Department of Materials Science and Engineering, University of Toronto, Toronto, Canada

Dalal Asker, Tarek S. Awad & Benjamin D. Hatton

Institute of Biomedical Engineering, University of Toronto, Toronto, Canada

Desmond van den Berg & Benjamin D. Hatton

Food Science & Technology Department, Alexandria University, Alexandria, Egypt

Dalal Asker

Physique et Mécanique des Milieux Hétérogènes, CNRS, ESPCI, PSL Research University, Sorbonne Université, Sorbonne Paris Cité, 75005, Paris, France

Nicolas Lavielle

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

D.V.D.B, D.A., N.L. and T.A. performed experiments. D.V.D.B., D.A., T.A. and B.D.H. wrote and reviewed the manuscript.

Correspondence to Benjamin D. Hatton.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

van den Berg, D., Asker, D., Awad, T.S. et al. Mechanical deformation of elastomer medical devices can enable microbial surface colonization. Sci Rep 13, 7691 (2023). https://doi.org/10.1038/s41598-023-34217-5

Download citation

Received: 13 October 2022

Accepted: 26 April 2023

Published: 11 May 2023

DOI: https://doi.org/10.1038/s41598-023-34217-5

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.