Antimicrobial properties of a multi

Scientific Reports volume 12, Article number: 21427 (2022) Cite this article

932 Accesses

1 Citations

2 Altmetric

Metrics details

High traffic touch surfaces such as doorknobs, countertops, and handrails can be transmission points for the spread of pathogens, emphasizing the need to develop materials that actively self-sanitize. Metals are frequently used for these surfaces due to their durability, but many metals also possess antimicrobial properties which function through a variety of mechanisms. This work investigates metallic alloys comprised of several metals which individually possess antimicrobial properties, with the target of achieving broad-spectrum, rapid sanitation through synergistic activity. An entropy-motivated stabilization paradigm is proposed to prepare scalable alloys of copper, silver, nickel and cobalt. Using combinatorial sputtering, thin-film alloys were prepared on 100 mm wafers with ≈50% compositional grading of each element across the wafer. The films were then annealed and investigated for alloy stability. Antimicrobial activity testing was performed on both the as-grown alloys and the annealed films using four microorganisms—Phi6, MS2, Bacillus subtilis and Escherichia coli—as surrogates for human viral and bacterial pathogens. Testing showed that after 30 s of contact with some of the test alloys, Phi6, an enveloped, single-stranded RNA bacteriophage that serves as a SARS-CoV-2 surrogate, was reduced up to 6.9 orders of magnitude (> 99.9999%). Additionally, the non-enveloped, double-stranded DNA bacteriophage MS2, and the Gram-negative E. coli and Gram-positive B. subtilis bacterial strains showed a 5.0, 6.4, and 5.7 log reduction in activity after 30, 20 and 10 min, respectively. Antimicrobial activity in the alloy samples showed a strong dependence on the composition, with the log reduction scaling directly with the Cu content. Concentration of Cu by phase separation after annealing improved activity in some of the samples. The results motivate a variety of themes which can be leveraged to design ideal antimicrobial surfaces.

Touch surfaces in high-traffic areas1,2,3 can become vectors for disease propagation through indirect contact between infected and vulnerable persons4,5, making it critical to develop self-sanitizing materials which are effective against a broad range of pathogens. Previous works have shown that microorganisms can remain alive or active on surfaces for hours to days6,7,8,9,10, including many human pathogens such as Methicillin susceptible Staphylococcus aureus (MSSA) and resistant Staphylococcus aureus (MRSA)11, Rhinovirus12, Influenza virus A13, Rotovirus14 and corona viruses such as the severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2)7,15, which has caused the global pandemic of 2020–202216,17. These long lifetimes partly determine the potential for pathogens to spread during subsequent contact with the surface18. High-traffic surfaces are often made of metals, with stainless steel (SS) being a common choice due to its relatively low cost, durability, and resistance to corrosion; SS has been reported to have modest antimicrobial properties19. Occasionally brass (CuZn), an alloy of copper and zinc, is employed for touch surfaces due to its pleasing golden hue, however it is a much softer metal, is more expensive—three times the cost of SS at the time of writing—and readily oxidizes; the green or black oxidation tends to exfoliate from the surface and so brass surfaces require regular cleaning. Brass has known antimicrobial activity20,21. Focusing on disease propagation, many of the metals which show antimicrobial activity22,23,24,25,26,27,28,29,30, such as copper (Cu), silver (Ag), and cobalt (Co), are not widely employed due to their cost and tendency to oxidize. Each of these metals achieves antimicrobial activity by different mechanisms against diverse pathogens18. By leveraging these mechanisms synergistically, a solid-solution alloy of these elements may be active against a range of pathogens larger than the sum of its parts, resulting in an antimicrobial super alloy.

This work focuses on the development of multicomponent alloys of CuAgCo; each of these metals achieve antimicrobial activity through different modes of action30. Copper in-particular has shown biological activity against a wide range of viruses7,22,23,24,2 protein *. J. Biol. Chem. 274, 5474–5482 (1999)." href="/articles/s41598-022-25122-4#ref-CR31" id="ref-link-section-d64682919e648">31 and bacteria7,30. The mode of action in these systems has been attributed to interactions between the Cu+1/+2 ions32 and surface proteins which become denatured, resulting in the viral envelope failing33,34. Silver metal has been used as an antimicrobial agent since times of antiquity35 and can bind with virus surface glycoproteins disrupting replication25,26,36,37. In bacteria, the sanitizing mechanisms in Ag have been attributed to damage to the cell wall and membranes38 and interference with internal cellular functions30,39. Cobalt in the Co3+ state has been reported to have anti-bacterial and anti-viral27,28,29 properties when complexed with chelators or ligands, potentially through Schiff bases, a mechanism that inactivates protein active sites40. In its un-oxidized state, cobalt has been shown to be effective at reducing bacterial presence39,41. By developing an alloy of these metals, the resultant material may show antimicrobial activity due to a range of mechanisms, making it simultaneously effective against a range of pathogens larger than any one metal. Furthermore, the multifaceted modes of action may provide accelerated sanitation properties.

A challenge to this work is that several of the binary alloys (CoCu, AgCo, AgNi and AgCu) do not mix to form alloys, e.g. they are immiscible42. To overcome this challenge, two approaches are used. In the first, room-temperature sputtering is used to achieve rapid solidification, freezing the atoms as an alloy before they are able to phase separate43,44. In the second approach, an entropy-based stabilization paradigm45,46 will be leveraged. This materials design concept proposes that increasing the chemical entropy within a multicomponent system increases the free energy cost of phase separation and thus can stabilize alloys of elements which are typically immiscible47. This approach has been used previously to realize new functional materials such as catalysts48 and magnets49,50. To increase the chemical entropy, an additional element, nickel (Ni), is added to form the four-component alloy CoCuAgNi; nickel does possess some antimicrobial activity of its own51 but was chosen primarily because it is miscible with both Cu and Co across their entire compositional range. In Ni-rich ternary compositions, CoCuNi forms a single-phase alloy. During thermal processing silicon (Si) is also introduced, diffusing from the substrate. Attempts were also made to further increase the entropy by including iron (Fe) and palladium (Pd), forming the five-component alloy CoCuAgFePd. A recent investigation has shown potential antimicrobial activity of a copper-containing high-entropy alloy (HEA) on two viruses52.

In the present study, thick-films of a proposed antimicrobial HEA CoCuAgNi(Si) are prepared by combinatorial sputtering and tested for their potential application as self-sanitizing surfaces. Combinatorial sputtering has been previously demonstrated as a high throughput approach to designing antimicrobial surfaces53,54,55. The antimicrobial activity of the as-prepared alloy is tested against four non-pathogenic surrogates representing infectious human pathogens including the bacteriophages Pseudomonas phage Phi6, which is similar in size and structure to SARS-CoV-2, including the surface spike proteins56, and the phage MS2, a non-encapsulated spike-less virus and a surrogate for the human novovirus57. Bacterial testing was performed on the Gram-positive Bacillus subtilis NRS 231 (ATCC: 6633) and the Gram-negative Escherichia coli strain Seattle 1946 (ATCC: 25,922), which served as surrogates for pathogenic bacterial strains. Next, the films were annealed and the antimicrobial activity re-examined. Annealing is important because a deployable metal for touch surfaces will likely be prepared by similar high temperature processing. For both the as-grown and annealed films, the nano- and microstructure is evaluated to test the HEA paradigm and assess the structure-performance relationship. In addition to the sputtered films, a range of related singe-component, binary and ternary surfaces are also investigated. This approach is designed to address the critical question of how the nanoscopic distribution of elements within a surface affects its antimicrobial activity.

Thin-films of (CoCuAgNi) alloy were prepared by combinatorial sputtering at room temperature on a 100 mm Si (100) wafer, as described in the Methods section, and shown illustratively in Supplementary Fig. S1. The sputtering technique uses an accelerated Ar plasma to generate a vapor of each metal at single-element sources. The elements blend in the vapor state and condense on the Si substrate, with solidification occurring on the nanosecond timeframe, offering little opportunity for the elements to diffuse. Without the opportunity to diffuse, the elements can form a metastable alloy, even if the parent elements are immiscible43,44. Evidence of alloying, rather than amorphous or glassy behavior, can be seen in the X-ray diffraction (XRD) data discussed below. For combinatorial sputtering specifically, the sputtering sources are arranged around the substrate in a confocal geometry; regions of the wafer close to (far from) a source have a higher (lower) concentration of the element from that target, thus a compositional gradient of ≈50% is achieved across the diameter of the wafer.

Compositional mapping was performed by scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDX), measured at 17 positions on the wafer. These maps, shown in Fig. 1a, identify the compositions at the four extremum edges of the sample to be (Ni11Ag21Co13Cu55) (Ni22Ag54Co6Cu18) (Ni26Ag12Co39Cu23) (Ni55Ag22Co12Cu11), with an equal compositional point located near the wafer center. X-ray diffraction measurements of the as-grown sample, Fig. 1b, show broad peaks at ≈39° (d = 2.31 Å) and ≈44° (d = 2.06 Å); these peaks align closely with the parent compounds: face centered cubic (FCC) Ag (111) at 37.4° (d = 2.40 Å), Ag (200) at 43.5° (d = 2.08 Å) and FCC Ni (111) at 44.8° (d = 2.02 Å). The similarity between these parameters suggests that the as-grown films possess an FCC structure with a polycrystalline microstructure. Also, for sufficient Ag content, the smaller (Co, Cu, Ni) atoms are integrated into the Ag crystal lattice. Decreasing the Ag content, the peak at ≈39° disappears, while the peak at ≈44° moves to higher angles, indicating the Ag is integrated into the smaller Ni lattice. The system is inherently strained due to the large difference in atomic size between the Ag (diameter of 160 pm), and the Ni, Co and Cu (≈135 pm)58. A crude measure of the structural phase distribution can be inferred from the ratio of the XRD peak areas, after correcting for the Fresnel fall off, the overlap of the Ag(200) and Ni(111), and the larger form factor from the Ag atoms. The resultant map of the phase distribution, Fig. 1c, confirms that the system undergoes a structural transition from the larger to smaller lattice spacing and at the equal composition point, the Ag is largely integrated into the CoCuNi lattice.

(a) Compositional map of Ni, Cu, Ag and Co. (b) X-ray diffraction patterns, taken at positions 1–17, identified in panel c. (c) Contour plot of the two FCC phases in the as-grown system.

After annealing at 600 °C for 60 min in flowing forming gas (N2 + 5%H2) the samples developed a foggy surface contrast while retaining a grey metallic hue, suggesting the they were not oxidized and are much rougher; annealing at 600° then cooling in air resulted in a blue colored oxide. X-ray diffraction measurements of the annealed films are shown in Fig. 2 and are indexed to three primary phases: Ag (FCC1), (Ni,Co)Si2 (fluorite, FCC2), and (Ni,Co,Cu)Si (B20). Previous works have shown that CoNi films grown on Si substrates and annealed in similar conditions uptake Si from the substrate, forming these phases59,60. Identification of these particular compositions were informed by previous works on NiCo/Si systems, and by comparison between the XRD and EDX results. All of the XRD patterns show peaks for an Ag-like (FCC1) phase with a lattice parameter of 4.077 Å, matching closely to bulk Ag (4.20 Å). EDX images in Fig. 3, taken at the equal composition point (identified as position 3 in the diagram) show ellipsoidal Ag precipitates ≈600 nm in diameter fully ejected from the film. While the HEA paradigm encourages alloying, it is not an absolute guarantee, as observed here. Returning to the conventional Hume-Rothery rules of alloy design, the maximal difference in atomic radii which can be accommodated in an alloy is 15%, while the difference between Ag and the other metals is > 18%; conventional materials design rules correctly predict the immiscibility of the Ag. Each of the binary phase diagrams also predict immiscibility of the 3d metals with Ag. Silver precipitates have been observed in previous antimicrobial surfaces of Ag-diamond like carbon (DLC), resulting in reduced materials longevity, but improved long-term antimicrobial properties54,61. The EDX also shows Ni and Co in the precipitates. The slightly smaller lattice parameter of FCC1 compared to bulk Ag is likely the result of a small amount of residual Ni and Co being alloyed into the lattice.

X-ray diffraction patterns captured at positions 1–17 after the anneal.

(a) Contour plot showing the relative XRD peak intensity for the FCC phases after the anneal, A(50°) / (A(47°) + A(50°)), where A is the peak area. (b) SEM and EDX images of positions 3, 8, and 1, identified in the contour plot. The scale bar in the SEM image corresponds to 1000 nm.

The film beneath the Ag precipitates is comprised of two distinct domains, identified by EDX as Cu-rich and Cu-poor; Cu-rich regions are also identified as Si-poor when compared to the Cu-poor domains. Initial considerations were that these were (Ni,Co) and (Ni,Co,Cu) alloys42,62, since the Si signal can also be from the substrate. However, the XRD results cannot be fitted using NiCoCu alloys, which are known to have a lattice parameter of ≈3.52 Å42. Previous works59,60 have shown that annealing NiCo on a Si wafer can rapidly form NiSi2, CoSi, and CoSi2, with heats of formation of − 50.73 kJ/mol, − 56.00 kJ/mol, and − 40.7 kJ/mol respectively. The current work is further complicated by the presence of Cu. The XRD peak at 47° can be exclusively indexed to the (220) peak of a NiSi2 fluorite structure, hereafter identified as FCC2, corresponding to a lattice parameter of 5.42 Å; this value is in good agreement with the parent compound, 5.44 Å. Similarly, the XRD peak at 50° can be associated exclusively with the (211) peak of a CoSi B20 structure, corresponding to a lattice parameter of 4.49 Å; this value is in good agreement with the parent compound, 4.43 Å. Using the diffraction peaks at 47° (red) and 50° (blue) the relative phase distributions are plotted in Fig. 3. The phase map confirms that, near the Ni edge the film is single-phase FCC2 (NiSi2), while in the NiCo corner, the film is single-phase B20 (CoSi). This phase distribution also gives rise to a distribution of the electronic structure of the film, with the disilicate FCC2 phase being predominantly charge neutral63, while the monosilicate B20 phase is tetravalent.

Recognizing that the Cu-rich and Si-poor regions are commensurate in the EDX images, the Cu is proposed to preferentially incorporate into the monosilicate B20 structure. Based on these results, the annealed sample can be generally described as a film, with domains of (Ni,Co)Si2 and (Ni,Co,Cu)Si, with (Ni,Co):Ag precipitates. The phase distribution map shows large, single-phase regions near positions 8 (B20) and 17 (FCC2). EDX images from position 8 show some chemical phase separation of the Cu, albeit less well-defined than position 3, despite that the XRD does not show structural phase separation. Micrographs were captured at seventeen points on the sample, approximately co-located with the XRD measurements; three representative positions are shown in Fig. 3 while the remaining images are provided in the Supplemental Materials Fig. S2.

Interesting microstructural changes occur approaching the extremums of the annealed wafer. Approaching the CoCu edge (position 14), the Ag does not precipitate as particles, but remains as part of the film, as a new domain. Approaching the Ag and AgCu edges (positions 1 and 6), the microstructure changes significantly, forming a worm-like lamella network suggesting at higher temperatures a single phase may exist and undergoes spinodal decomposition into Ag- and Cu-rich phases. The lamellae are much smaller than the domains or precipitates in the rest of the film, with widths of ≈65 nm. The different structures, particularly of the Ag, may result in different strengths of antimicrobial activity64. These results suggest that Ag-rich and CoCu-rich compositions may be prepared as bulk alloys, and retain all of the elements in localized alloy domains. The following sections investigates the antimicrobial activity of the as-grown wafer (with the elements uniformly intermixed on an atomic scale), and the annealed wafer (with compositional domains and Ag precipitates).

A range of single-component metals, including Co, Cu, Ni and Ag, among others, were tested for antimicrobial activity against the surrogate microbes. Metals for the single-component tests were included due to their reported antimicrobial activity against a variety of human pathogens30 or commercial availability. Prior to testing, surfaces were cleaned with acetone to remove any contaminating microbes or grease, but leaving the native oxide layer which would be expected on a deployed touch surface. Testing was performed by spotting 10 µL of a concentrated aqueous solution containing the test organism onto a 25 × 25 mm2 test surface, covering the spot with a 25 × 25 mm2 sterile glass slide, then recovering the microorganisms by washing the surface, and enumerating the live microorganisms, as described in the Methods, and shown illustratively in Supplementary Fig. S3. This methodology was developed based on previous works65,66. Testing times were chosen based on the minimum time necessary to achieve complete sanitation with the Cu positive control—within the limits of the measurement procedure. This testing methodology is designed to simulate wet contact, for example, microorganisms in droplets from breathing, sneezing or coughing and does not represent ‘dry’ contact assays. The metal Cu had significant (p > 0.05) antimicrobial activity against Phi6 and MS2, Fig. 4a,b (and Supplemental Fig. S4), achieving a 6.9-log reduction of Phi6 (30 s test time) and a 7.1-log reduction for MS2 (30-min test time). The log-reduction metric is a percentile scale which is normalized to the titer concentration for each test; these values correspond to the limits of detection for each respective organism. All of the other tested metals—including our candidate metals Co, Ni and Ag—showed much lower activity. Also notable among the tested metals is zinc (Zn), which has been previously reported to have antimicrobial activity against a wide range of pathogens30, but here appears to be weak (Supplementary Fig. S5). Zinc was not used in the wafer due to its high vapor pressure, making it incompatible with general-use vacuum systems. All of the tested surfaces, other than Cu, are statistically identical to the stainless steel (alloy 304) control; 304SS is chosen as the control due to its common use for high-traffic surfaces.

Antimicrobial activity of single component (left) and multicomponent (right) surfaces, tested on (a, e) Phi6, (b, f) MS2, (c, g) E. coli, and (d, h) B. subtilis. No B. subtilis was recovered on the metal Cu.

The gram-negative model Escherichia coli and gram-positive model Bacillus subtilis were also tested on the single-component surfaces, Fig. 4c,d, respectively. These measurements again show strong activity from Cu. Testing times were established based on the full sanitation of the Cu control surface; rarely, an active Phi6, MS2 or live e. coli was recovered due to statistical variation, however, no B. subtilis was recovered on any Cu control surface after the initial setting of the measurement time. While E. coli experienced a significant 5.9-log reduction after 20 min of contact, corresponding to only one colony enumerated in the highest concentration wash. In all of the bacterial assays the Ag, Co and Ni were again statistically indistinguishable from the SS control. These results suggest that surface contact of these bulk materials may be insufficient to impart antimicrobial activity in the timeframe tested here. Overall, Cu was the most effective metal at reducing microbial activity in both the phages and bacteria. This strong activity motivated its use as the positive control in subsequent assays.

Two alloys of brass (alloy 360, Cu0.6Zn0.4 and alloy 260, Cu0.7Zn0.3) were also examined in contact assays, Fig. 4e–h; these alloys contained both antimicrobial materials Cu and Zn (Supplementary Fig. S6). Assays performed with Phi6 on alloy 260 and 360 resulted in no countable plaques after 30 s of exposure, identical to pure Cu. For the other phage, MS2, the antimicrobial activity was superior when compared to any of the single-component surfaces except pure Cu; alloy 260 achieved a log reduction of 5.3, while alloy 360 achieved a log-reduction of 4.0. Assays performed on the bacteria showed a similar trend, with the Cu-rich alloys displaying strong antimicrobial activity: E. coli showed a log-reduction of 5.6 on alloy 260 and no bacteria were recovered on alloy 360, while B. subtilis experienced a log-reduction of 4.5 and 5.2 on alloys 260 and 360, respectively.

The above results together support a theme that Cu-content strongly influences the antimicrobial activity in contact assays. In a deployed surface, the Cu is expected to be oxidized and present as either divalent CuO or monovalent Cu2O. While the tested Cu coupons have a native oxide layer, this is expected to be a mix of the two states. Oxidized Cu can be prepared in either state by annealing Cu coupons in air as described previously67. Coupons were prepared with CuO and Cu2O oxidized surfaces. Contact assays performed on oxidized coupons of CuO, Fig. 4e–h, showed comparable antimicrobial activity to pristine copper, with log reductions of 6.5 and 4.8 for Phi6 and MS2, and no E. coli or B. subtilis were recovered. The Cu2O films still showed antimicrobial activity, but tended to be more microbe-specific, with log reductions of 2.8, 4.9, 5.8, and 4.5 for Phi6, MS2, E. coli and B. subtilis, respectively. These results suggest that the divalent (Cu+2) oxide possesses stronger antimicrobial properties than the monovalent (Cu+1).

In the final preliminary investigation, the antimicrobial activity of Cu-containing alloy (Cu55Zn28Ni14Mn2) was evaluated. This alloy is a candidate material for next-generation minted currency68, making it highly relevant as a high-traffic touch surface. Current coins in circulation in the United States are alloys of Ni (8.3% or 25%) and Cu, or are Cu-coated in the case of the penny. Contact assays showed significant (p < 0.05) activity against Phi6 (log reduction of 3.2) and E. coli (4.5) (Supplemental Fig. S4). However, the antimicrobial activity against MS2 (2.0) and B. subtilis (0.5) was statistically identical to the 304 stainless steel control. This alloy is similar in composition to brass alloy 360, however, its antimicrobial activity is significantly less, suggesting the Cu-content is not the only motivator of activity.

Thin films comprised of the antimicrobial metals Cu, Ag, Co and Ni were prepared by sputtering and segmented into eight coupons, corresponding to labels 1–8 in Fig. 5a, for testing in contact assays; the composition at the center of each coupon is listed in Table 1. As noted above, the rapid transformation from the gas phase to a solid film which is achieved with the sputtering technique prepares the as-grown film as a homogenized alloy43,44. The antimicrobial activity of each coupon was used in the preparation of a heatmap, shown for each organism in Fig. 5, with the quantitative bar-graph representation shown in the Supplemental Fig. S6. For Phi6, treatments with chips 2 and 5 resulted in the largest reductions of activity (p < 0.05), nearly at the limit of detection and comparable to pure Cu. Antimicrobial activity sequentially decreased in coupons 6, 3, 8, 4, 7, and 1. Comparing Fig. 5a with Fig. 1a, the antimicrobial activity (log reduction) against Phi6 closely follows the Cu content. Testing against the phage MS2 (Fig. 5b) had a similar trend, with coupons 5, 2, and 3 showing the strongest activity (defined as comparable to pure Cu) and decreasing with the Cu content. The coupons showed broader activity against E. coli and B. subtilis, Fig. 5c,d, respectively, with coupons 2, 5, and 6 showing strong antimicrobial activity. For E. coli the antimicrobial activity continued to show a direct dependence on the Cu content, similar to Phi6 and MS2, however, the heat map suggests that the most-active composition against B. subtilis is near the equacompositional point.

Heat map of log-reduction on the thin film chips of (a) Phi6, (b) MS2, (c) E. coli, and (d) B. subtilis; log-reduction on the annealed chips of (e) Phi6, (f) MS2, (g) E. coli, and (h) B. subtilis.

Across all of the testing, coupon #1 (Cu23Co40Ni25Ag12) showed the least antimicrobial activity. This is notable because the heat plots tend to indicate a strong dependence on Cu content, however coupon #1 was not the lowest Cu composition, coupons 4, 7 and 8 were all lower; coupon #1 has the largest Co content (40%). This result again suggests that Cu levels are not completely driving the alloy's activity. Finally, none of the plots show any sensitivity of the structural distribution shown in Fig. 1c.

The thin films were annealed, resulting in the phase separation discussed above and shown in the micrographs in Fig. 3, then tested for antimicrobial activity. Testing results are shown in heat maps, Fig. 5e–h, and in bar graphs in the (Supplemental Fig. S7). Testing on Phi6, Fig. 5e, again showed strong activity from coupon 2 which was statistically identical to the as-grown coupon 2. However, coupon 5 had a statistically significant reduction in antimicrobial activity against Phi6 (p < 0.05) compared to its as-grown alloyed counterpart. All of the other chips showed increased activity after annealing, however only chip 7 showed a statistically significant increase (p < 0.05).

The heatmaps for MS2 and E. coli show activity trends which are similar between the as-grown and annealed samples. Against MS2 the annealed wafer shows slightly increased activity, while E. coli shows a slight decrease. However, neither trend showed a statistically significant difference between the as-grown and annealed test surfaces.

Finally, B. subtilis was tested and the coupons 2 and 5 again showed significant activity (Fig. 5h and S7). However, in contrast to the other pathogens, the other coupons showed a large reduction in activity relative to the alloyed sample. Coupons 1 and 3 still showed stronger activity compared to the SS control, while the remaining coupons (8, 6, 7, and 4) were statistically identical to the SS control. The annealing process led to a significant loss of antimicrobial activity on the chips 3, 6, 4, and 7 (p < 0.05), which were from the Ni and Co heavy regions, when compared to the as-grown chips.

The above data shows the antimicrobial activity of contact surfaces for a variety of common engineering materials and an alloyed and phase-separated thin-film. Four metals were chosen based off their previously reported antimicrobial activity (copper, cobalt, nickel, and silver) and prepared as an alloyed thin-film which were then annealed, resulting in Si uptake and phase separation. While the materials design paradigm proposed to realize an alloy, stabilized by its chemical entropy, the phase separation shows that this was unsuccessful, the annealing resulted in phase separation. However, this allowed testing of the role of microstructure and chemical distribution. Contact viability assays were performed on two surrogate bacteriophages and two bacteria, representative of common human pathogens.

The prevailing theme throughout the measurement was the overwhelming antimicrobial activity of copper against every surrogate organism. On pure Cu, Phi6, the SARS-CoV-2 surrogate was inactivated by nearly 7 orders of magnitude to after only 30 s. Each of the other three microorganisms were also significantly reduced to the limit of detection after < 30 min. The strong antimicrobial activity of Cu is consistent with previous reports32,34. Several mechanism of action have been proposed to support the antimicrobial activity of Cu, including membrane disruption, enzyme inactivation, the generation of reactive oxygen species, and the denaturing genetic material. In comparison, the non-copper containing metals and oxides individually reduced all of the microorganisms’ activity by approximately a single order of magnitude over the same testing time. These results were unexpected due to the well-known antimicrobial activity of Zn and Ag in-particular. This may be the result of the microstructure which appears to be related to the antimicrobial activity, especially for Ag. These metals were not treated before testing, and so likely have a native oxide layer, which may reduce their activity. However, much of the reported antimicrobial activity emphasizes the role of the cation, which typically has an oxidation state of + 2 and would be found in many of these native oxide surfaces.

The antimicrobial activity of Cu and its two common oxides, CuO and Cu2O, representing divalent and monovalent Cu, respectively, were tested. Both oxides showed strong activity, with the monovalent Cu2O being slightly less effective against Phi6 (p < 0.05). The distinction between the two copper oxides is the valence state of the copper, Cu2+ for CuO and Cu1+ for Cu2O. Previous works have emphasized the critical role of Cu ions in achieving antimicrobial activity against microorganisms. For example, in viral assays, Cu1+ ions were responsible for generating hydroxyl radicals that led to the deactivation of the influenza virus32 and Cu2+ showed activity against enveloped and non-enveloped viruses69. While in bacterial systems, Cu1+ is reported to be more toxic to bacteria32 and can initiate redox cycling which can damage key cellular processes. Due to the short testing time frame it is unlikely that the microbes caused surface corrosion, particularly since there was no observed drop in activity of the metal controls70,71. Next, two brasses were tested: alloy 360 (Cu0.6Zn0.4) and alloy 260 (Cu0.7Zn0.3). Alloy 260, which has higher Cu content, had stronger antimicrobial activity and statistically identical within our assay to pure Cu. Finally, a currency prototype which is similar to brass, Cu55Zn28Ni14Mn2, showed moderate antimicrobial activity against Phi6 and E. coli, but weak activity against MS2 and B. subtilis. This was surprising because the currency has a similar composition as brass alloy 360, but replaces 14% of the Zn with Ni. The Ni is included for its anticorrosion qualities, supporting the idea that the oxidized surface is important to achieve antimicrobial activity.

Considering the antimicrobial activity of the as-prepared (alloyed) thin-film, the data suggests that, for all the organisms, the Cu content is a primary factor in the antimicrobial activity. The antimicrobial activity of the alloyed wafer against Phi6 (Fig. 5a) is plotted going away from the Cu target across the equatorial ray of the wafer in Fig. 6a. This data is expected to be sigmoidal, with both high- and low-concentrations of Cu having little dependence on the at.% Cu. Indeed, the data was well fitted with a variety of sigmoidal functions, with a 5-parameter Logistic function shown in the figure. Notably, the region 10–65 at.%, which represent the composition explored on the wafer, is highly linear; a fit to this data returns a line: Log(A) = 0.094 x + 1.04, where A is the total antimicrobial activity and x is the at.% Cu. This equation can be arranged to solve for the total activity: \(A={A}_{0}{e}^{cx}\), where the intercept (x = 0) corresponds to the inherent activity at 0% Cu (A0 = 10.9, corresponding to a log reduction of 1.04), and c is a copper-derived antimicrobial activity correlation constant (0.094). The value for A0 agrees well with the activity of the stainless steel, which showed a reduction of A = 9.6 (log reduction of 0.98) for Phi6 over the test time frame. Agreement in these values supports the relative inactivity of stainless steel.

Line-cuts of the antimicrobial activity for (a) Phi6, (b) MS2, (c) E. coli, and (d) B. subtilis, taken across the equatorial ray of the wafers between Cu and Ni.

Another important feature of the alloy data is that, within the investigated compositional range (10–65 at.%), the data does not show any flattening at high or low concentrations. This is notable because it implies that, even in relatively dilute concentrations the copper still contributes to the antimicrobial activity. In other words, the critical density of copper to achieve some antimicrobial activity is less-than 10 at.%—the lowest concentration tested here.

While the alloyed wafer shows a clear dependence on the Cu content, the annealed sample, also plotted in Fig. 6a, is much less clear. The ray for the annealed sample shows an appreciable drop in activity for the high-concentrations and increased activity for the low-concentrations. This difference can be understood by considering the phase separation reported above. Specifically, the EXD images (Fig. 3) showed that the Cu is concentrated into specific chemical domains of the film, resulting in Cu-rich and Cu-poor domains. As a result, the effective areal coverage of the copper on the film goes down. However, the Cu-rich domains will show exponentially increased activity, as shown from the alloyed samples. Since the antimicrobial activity depends exponentially on the Cu content, while the areal coverage changes linearly, the resulting antimicrobial activity in the annealed samples is increased. However, at higher concentrations of Cu, the antimicrobial activity is already exceedingly strong, such-that additional Cu concentration does not increase activity. That is, the sigmoidal fit shows that increasing the Cu concentration beyond 65 at.% does not significantly increase the antimicrobial activity on the tested timeframes—the phages are already inactivated. Therefore, the phase separation contributes only by decreasing the areal coverage and hence reduces the apparent antimicrobial activity.

The other organisms are shown in Fig. 5b–d. Of these, MS2 shows a similar, albeit weaker, trend to Phi6, with decreased (increased) activity after annealing at higher (lower) Cu concentrations. E. coli showed a slight (not statistically significant) increase in activity in the annealed sample, but in general the trend changed very little. Finally, B. subtilis showed a significant decrease in activity with annealing. One possible reason for this decrease in activity is the large size of B. subtilis, which is 4–10 µm in length and 0.5 µm in diameter, compared to E. coli, which is 1–2 µm in length and 0.5 µm in diameter. Both of these length scales are larger than the chemical domains (≈700 nm) after phase separation, however the B. subtilis may be large enough that it is able to isolate the copper damaged regions. Important to note, in this plot, at high concentrations of Cu, the wafer is able to fully kill the bacteria.

Figure 6 also shows that the testing time for each organism (30 s for Phi6, 30 min for MS2, 20 min for E. coli, and 10 min for B. subtilis) captures a range of efficacies, including fully sanitizing. The significant differences between these testing times may highlight critical physiological differences between the microorganisms which determine their susceptibility to the metallic surface. Specifically, Phi6, the enveloped phage, had the shortest testing time and is thus most susceptible to attack by the Cu in the surface. This may indicate that Cu, or the native oxides, rapidly degrades the envelope membrane or easily passes through the membrane, resulting in inactivation. The much longer (60 × longer) testing times for the MS2 suggests that the protein capsid which surrounds MS2 provides significant protection against the antimicrobial properties of the Cu. Another key difference between Phi6 and MS2 is that Phi6 has spike proteins, which are responsible for binding to the bacterial host, while MS2 has no such structure. The antimicrobial activity of the Cu may be achieved by degrading, or otherwise denaturing, the structure of the spike proteins, achieving rapid inactivation.

Comparing the bacteria, the test times are also much longer than Phi6, but this may simply be a consequence of their much larger size. Between E. coli and B. subtilis, the shorter testing time of B. subtilis, which is also a larger bacteria, suggests it is more susceptible to the contact-based antimicrobial activity. This is somewhat surprising because B. subtilis is the gram-positive surrogate, meaning it has an exterior cell wall, comprised of peptidoglycan enmeshed with wall teichoic and lipoteichoic acids, which collectively from sheets of anionic charge. These layers act as a semi-permeable barrier that regulates cation movement, through binding, and is expected to protect the more-fragile membrane from the reactive metallic surface72. Further studies beyond the scope of this work are necessary to elucidate the various modes of action in these systems.

In summary, this work investigated a range of materials as candidate antimicrobial, high-traffic touch surfaces73. Four specific metals (Co, Ni, Cu and Ag) were chosen based off previous literature, and prepared as a thin-film medium-entropy alloy. Upon annealing, the alloy took up Si from the substrate and phase separated into Ag, Cu-rich and Cu-poor regions. The candidate materials were tested against four microorganisms which are surrogates for common viral and bacterial human pathogens. The collective results emphasize the overwhelming antimicrobial activity from Cu. Key results were that (1) Cu was an effective antimicrobial agent even at low concentrations, (2) the inclusion of anti-corrosion elements tended to suppress antimicrobial activity, and (3) the antimicrobial activity was exponentially dependent on the Cu concentration. This last result was balanced against the areal density of Cu in the phase separated (annealed) films, increasing the antimicrobial activity without adding further Cu. Complementary to these conclusions, the absence of synergistic activity, particularly in the alloy, is an important observation. While further testing must be performed to identify qualities that are important to a deployable alloy (such as wear resistance and allergenic response to the included Nickel), these results provide important insights into the role of microstructure in designing such a material. Together, these results demonstrate copper containing alloys as effective antimicrobial touch surfaces and offers a variety of insights supporting the development of effective sanitizing surfaces.

Some single-element and binary alloys were purchased from McMaster Carr, including Sn, Cu, SS304, Brass 360 (Cu60Zn40) and Brass 260 (Cu70Zn30); these were industry grade materials. Silver plate (99.9%) was purchased from Sigma Aldrich. The Si sample was a semiconductor-grade (100) single crystal wafer. SiO2 was a fused silica microscope slide. All materials were used as received without any surface treatments. Copper oxides (I) and (II) were prepared by annealing plate copper in air at 300 °C and 350 °C, respectively, for 3 h, then passively cooling to room temperature, also in air.

Combinatorial wafers were prepared by magnetron sputtering in an Ar atmosphere from single-element sources, confocally oriented around an (001) Si wafer with native oxide coating. Deposition was performed at room temperature. The wafer was not rotated during deposition, resulting in compositional gradients across the sample with a target film thickness of ≈200 nm. Compositions were controlled by adjusting the power to the sputtering sources, resulting in an approximately equacompositional point located at the center of the wafer. Precise measurement of the compositions was determined using electron dispersive X-ray spectroscopy (EDX) at 17 points along eight directions oriented radially from the wafer center. These measurements also captured element-specific plane-view maps of the local compositional distribution. Four as-grown wafer alloys were prepared, one for each surrogate microorganisms. Annealed samples were then heated in vacuum (< 10−6 Torr) or forming gas (4% H2 in N2) to 600 °C and held for 1 h, then allowed to passively cool overnight.

X-ray diffraction (XRD) measurements were performed using a Cu K-α (λ = 1.5406 Å) source. The sample rotation axis (θ) was fixed and the sample illuminated with a spot-like beam, as the 2θ axis was swept from 20° to 80°. The spot-like beam was produced using a snout with a 5 mm diameter aperture. The sample was then translated, and the measurement repeated, capturing the XRD pattern from 17 points, approximately coinciding with the EDX measurements.

Scanning electron microscopy (SEM) was performed on the as-grown and annealed samples using an acceleration voltage of 15 keV and a backscattered electron detector. Energy dispersive X-ray spectroscopy (EDX), including the spectrum and spatial mapping, was performed using a cryogen-free silicon drift detector.

The prototype currency composition was 14.4 wt. % Ni, 28.1 wt. % Zn, 2.3 wt. % Mn, balance Cu. Only a single coin was available for contact testing. The initial purities of the pure element starting materials were 0.9995 + Cu, Ni, and Zn, and 0.99 + Mn. Sheets of the commercial alloys C71300 (Cu-25Ni) and C77000 (Cu-18Ni27Ni)3 were provided by the US Mint for characterization and comparison with the designed prototype alloys. Coins were prepared as described by Lass et al.68.

The bacteria Pseudomonas Syringae var. phaseolicola (Félix d'Hérelle Reference Center for Bacterial Viruses, University of Laval, QC Canada) was used for phage titering and phage propagation of Psuedomonas phage Phi6. Escherichia Coli C3000 (ATCC 15597, American Type Culture Collection, VA USA) was used for phage titering and phage propagation of the E.coli phage MS2 (ATCC 15597-B1). Escherichia coli FDA strain Seattle 1946 (ATCC 25922) was used as the model gram negative strain for bactericidal testing. Bacillus subtilis subsp. spizizenii NRS 231 (ATCC 6633) was used as the model gram positive strain for bactericidal testing. All strains were stored at − 80 °C in Brain Heart Infusion (BHI) supplemented with 15% (wt/vol) glycerol. Cultures of P. syringae were grown on Lysogeny Broth (LB) agar plates at 25 °C. Overnight cultures were inoculated with a single colony from a streak plate into LB broth and grown at 25 °C in a shaking water bath at 160 RPM. Both E. coli strains were grown on LB agar plates at 37 °C, and overnight cultures were prepared as previously described and incubated at 37 °C. B. subtilis cultures were grown on BHI agar plates at 37 °C, and overnight cultures were prepared in BHI media and grown at 37 °C.

Phage stocks for this project were amplified by the plate lysate method. An aliquot of overnight culture (30 μL for MS2 and 300 μL for Phi6) and 100 μL of the phage dilution in pH 7.4 phosphate buffered saline (PBS) was aliquoted into 3–3.5 mL of LB overlay agar after equilibrating to 45 °C. The mixture was vortexed briefly, poured onto the agar underlay and allowed to solidify for 20–30 min. Plates were then incubated for 18–24 h at 25 °C for Phi6 or 37 °C for MS2. Five mL of sterile PBS was aliquoted onto each plate with confluent lysis and allowed to sit for 1–2 h. The buffer was then removed from the plate with a serological pipette, centrifuged at 5000 g for 10 min at 4 °C to remove debris, and then filter sterilized using a 0.20 μm-pore size surfactant-free cellulose acetate (SFCA) syringe filter (Corning, Incorporated, Corning, NY). This filter sterilized stock was then concentrated by centrifugation at 12,000 g for 2 h, the supernatant was removed by serological pipet and the phage pellet was resuspended in sterile PBS by static incubation overnight at 4 °C. Master stocks of Phi6 were stored at − 80 °C in PBS supplemented with 15% (v/v) glycerol, working stocks were prepared by plate lysate and centrifuge concentration from freshly thawed master stock prior to each experiment and stored short-term at 4 °C. All stocks of MS2 were stored at 4 °C.

Bacterial stocks for bactericidal testing were prepared by inoculating a 5 mL tube of the appropriate growth media 1:100 with an overnight culture of the test bacteria and incubated in a shaking water bath at the 37 °C at 160 RPM until the OD600 reached 0.2. The culture was then centrifuged at 5000 g for 10 min, the supernatant was discarded and the bacterial pellet was resuspended in 500 μL of PBS and immediately used for testing.

Antimicrobial activity was determined through contact assay testing, adapted (with modification) from the methods described in Haldar et al. and Nakajo et al. 65,66. All preparation and testing took place in a class II biosafety cabinet. Prior to exposure all test materials were briefly washed in acetone, and once dried each material was placed into a 60 × 15 mm sterile petri dish. Each microorganism was exposed to fresh (untested) coupons of Cu, Ag, Ni, Co, oxides and brass (2.5 × 2.5 cm2). The alloy wafers were segmented into 8 chips that were 2.5 × 2.5 cm2 in size and each microorganism was tested on a single set of chips. All contact assays were conducted in triplicate and on separate occasions. To conduct the assay 10 μL of a working stock of the test microbe was spotted on to center of the test material, covered by a 25 × 25 mm2 square glass slide and incubated at room temperature for the designated exposure time: Phi6 30 s, MS2 for 30 min, E. coli for 20 min, and B. subtilis for 10 min. After the exposure time had elapsed, the slide was separated from the test material by 70% ethanol-decontaminated forceps, and both the test material and slide were washed three times with a single 990 μL aliquot of PBS into the petri dish. The wash was immediately collected into a sterile 1.5 mL microcentrifuge tube, and then serially diluted in PBS and enumerated by double-layer agar plating for phages and by spread plating for bacteria; enumeration was performed with 100 μL of the diluted solution. After testing, all materials were immediately decontaminated in 70% ethanol for 30 min, then rinsed with deionized water, dried, and rinsed with acetone before storage under vacuum.

To evaluate the efficacy of each metal treatment the log reduction was calculated from the raw phage and microbial counts. A Shapiro-Wilks test was conducted and if the data did not meet the assumptions of normality, a rank transformation was applied. A one-way analysis of variance (ANOVA) (p < 0.05) was conducted on the data (normal and transformed) to determine any significant differences with the statistical software JMP Pro 14.2 (SAS Institute, Cary, NC).

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

Lopez, G. U. et al. Transfer efficiency of bacteria and viruses from porous and nonporous fomites to fingers under different relative humidity conditions. Appl. Environ. Microbiol. 79, 5728–5734 (2013).

Article ADS CAS Google Scholar

Pietsch, F. et al. Selection of resistance by antimicrobial coatings in the healthcare setting. J. Hosp. Infect. 106, 115–125 (2020).

Article CAS Google Scholar

Chang, T. et al. A novel methodology to study antimicrobial properties of high-touch surfaces used for indoor hygiene applications—A study on Cu metal. PLoS ONE 16, e0247081 (2021).

Article CAS Google Scholar

Otter, J. A. et al. Transmission of SARS and MERS coronaviruses and influenza virus in healthcare settings: the possible role of dry surface contamination. J. Hosp. Infect. 92, 235–250 (2016).

Article CAS Google Scholar

Reynolds, K. A., Watt, P. M., Boone, S. A. & Gerba, C. P. Occurrence of bacteria and biochemical markers on public surfaces. Int. J. Environ. Health Res. 15, 225–234 (2005).

Article CAS Google Scholar

Kuhn, P. J. Doorknobs: a source of nosocomial infection. Diagn. Med. 6, 62–63 (1983).

Google Scholar

Van Doremalen, N. et al. Aerosol and surface stability of SARS-CoV-2 as compared with SARS-CoV-1. N. Engl. J. Med. 382, 1564–1567 (2020).

Article Google Scholar

Kramer, A., Schwebke, I. & Kampf, G. How long do nosocomial pathogens persist on inanimate surfaces? A systematic review. BMC Infect. Dis. 6, 130–130 (2006).

Article Google Scholar

Gordon, Y. J., Gordon, R. Y., Romanowski, E. & Araullo-Cruz, T. P. Prolonged recovery of desiccated adenoviral serotypes 5, 8, and 19 from plastic and metal surfaces in vitro. Ophthalmology 100, 1835–1840 (1993).

Article CAS Google Scholar

Bueckert, M., Gupta, R., Gupta, A., Garg, M. & Mazumder, A. Infectivity of SARS-CoV-2 and other coronaviruses on dry surfaces: potential for indirect transmission. Materials 13, 5211 (2020).

Article ADS CAS Google Scholar

Kramer, A. & Assadian, O. Survival of microorganisms on inanimate surfaces. In Use of Biocidal Surfaces for Reduction of Healthcare Acquired Infections 7–26 (Springer, Cham, 2014).

Chapter Google Scholar

Reed, S. E. An investigation of the possible transmission of rhinovirus colds through indirect contact. Epidemiol. Infect. 75, 249–258 (1975).

CAS Google Scholar

Sze-To, G. N., Yang, Y., Kwan, J. K. C., Yu, S. C. T. & Chao, C. Y. H. Effects of surface material, ventilation, and human behavior on indirect contact transmission risk of respiratory infection. Risk Anal. 34, 818–830 (2014).

Article Google Scholar

Ansari, S., Sattar, S., Springthorpe, V., Wells, G. & Tostowaryk, W. Rotavirus survival on human hands and transfer of infectious virus to animate and nonporous inanimate surfaces. J. Clin. Microbiol. 26, 1513–1518 (1988).

Article CAS Google Scholar

Poggio, C. et al. Copper-alloy surfaces and cleaning regimens against the spread of SARS-CoV-2 in dentistry and orthopedics. From fomites to anti-infective nanocoatings. Materials 13, 3244 (2020).

Article ADS CAS Google Scholar

Van Damme, W. et al. The COVID-19 pandemic: diverse contexts; different epidemics-how and why?. BMJ Glob. Health 5, e003098 (2020).

Article Google Scholar

Who, S. A. WHO coronavirus disease (COVID-19) dashboard (World Health Organization, 2020).

Google Scholar

Imani, S. M. et al. Antimicrobial nanomaterials and coatings: current mechanisms and future perspectives to control the spread of viruses including SARS-CoV-2. ACS Nano 14, 12341–12369 (2020).

Article CAS Google Scholar

Geng, P. et al. Comparison of antibacterial ability of copper and stainless steel. Front. Chem. China 2, 209–212 (2007).

Article Google Scholar

Grass, G., Rensing, C. & Solioz, M. Metallic copper as an antimicrobial surface. Appl. Environ. Microbiol. 77, 1541–1547 (2011).

Article ADS CAS Google Scholar

Różańska, A. et al. Antimicrobial properties of selected copper alloys on staphylococcus aureus and escherichia coli in different simulations of environmental conditions: With vs. without organic contamination. Int. J. Environ. Res. Public Health 14, 813 (2017).

Article Google Scholar

Chruściński, L. et al. Specific interactions of Cu2+ ions with fragments of envelope protein of hepatitis B virus. J. Inorg. Biochem. 63, 49–55 (1996).

Article Google Scholar

Roth, E. J. et al. Metal thiolate coordination in the E7 proteins of human papilloma virus 16 and cottontail rabbit papilloma virus as expressed in Escherichia coli. J. Biol. Chem. 267, 16390–16395 (1992).

Article CAS Google Scholar

Almazán, F., Tscharke, D. C. & Smith, G. L. The vaccinia virus superoxide dismutase-like protein (A45R) is a virion component that is nonessential for virus replication. J. Virol. 75, 7018–7029 (2001).

Article Google Scholar

Sondi, I. & Salopek-Sondi, B. Silver nanoparticles as antimicrobial agent: A case study on E. coli as a model for Gram-negative bacteria. J. Colloid Interface Sci. 275, 177–182 (2004).

Article ADS CAS Google Scholar

Kim, J. S. et al. Antimicrobial effects of silver nanoparticles. Nanomed. Nanotechnol. Biol. Med. 3, 95–101 (2007).

Article CAS Google Scholar

Liu, X., Ropp, S. L., Jackson, R. J. & Frey, T. K. The rubella virus nonstructural protease requires divalent cations for activity and functions in trans. J. Virol. 72, 4463–4466 (1998).

Article CAS Google Scholar

Olejniczak, M. et al. The bulge region of HIV-1 TAR RNA binds metal ions in solution. Nucleic Acids Res. 30, 4241–4249 (2002).

Article CAS Google Scholar

Okada, A., Miura, T. & Takeuchi, H. Zinc- and pH-dependent conformational transition in a putative interdomain linker region of the influenza virus matrix protein M1. Biochemistry 42, 1978–1984 (2003).

Article CAS Google Scholar

Chaturvedi, U. C. & Shrivastava, R. Interaction of viral proteins with metal ions: role in maintaining the structure and functions of viruses. FEMS Immunol. Med. Microbiol. 43, 105–114 (2005).

Article CAS Google Scholar

Gandhi, C. S. et al. Cu(II) inhibition of the proton translocation machinery of the influenza A virus M₂ protein *. J. Biol. Chem. 274, 5474–5482 (1999).

Article CAS Google Scholar

Vincent, M., Duval, R. E., Hartemann, P. & Engels-Deutsch, M. Contact killing and antimicrobial properties of copper. J. Appl. Microbiol. 124, 1032–1046 (2018).

Article CAS Google Scholar

Cortes, A. A. & Zuñiga, J. M. The use of copper to help prevent transmission of SARS-coronavirus and influenza viruses. A general review. Diagn. Microbiol. Infect. Dis. 98, 115176–115176 (2020).

Article CAS Google Scholar

Warnes, S. L. & Keevil, C. W. Inactivation of norovirus on dry copper alloy surfaces. PLoS ONE 8, e75017 (2013).

Article ADS CAS Google Scholar

Abram, S.-L. & Fromm, K. M. Handling (nano)silver as antimicrobial agent: therapeutic window, dissolution dynamics, detection methods and molecular interactions. Chem. Eur. J. 26, 10948–10971 (2020).

Article CAS Google Scholar

Naik, K. & Kowshik, M. The silver lining: Towards the responsible and limited usage of silver. J. Appl. Microbiol. 123, 1068–1087 (2017).

Article CAS Google Scholar

Elechiguerra, J. L. et al. Interaction of silver nanoparticles with HIV-1. J. Nanobiotechnol. 3, 6 (2005).

Article Google Scholar

Yin, I. X. et al. the antibacterial mechanism of silver nanoparticles and its application in dentistry. Int. J. Nanomed. 15, 2555–2562 (2020).

Article CAS Google Scholar

Yasuyuki, M. et al. Antibacterial properties of nine pure metals: A laboratory study using Staphylococcus aureus and Escherichia coli. Biofouling 26, 851–858 (2010).

Article CAS Google Scholar

Murray, A. F., Satooka, H., Shimizu, K., Chavasiri, W. & Kubo, I. Polygonum odoratum essential oil inhibits the activity of mushroom derived tyrosinase. Heliyon 5, e02817 (2019).

Article Google Scholar

Chang, E. L., Simmers, C. & Knight, D. A. Cobalt complexes as antiviral and antibacterial agents. Pharmaceuticals (Basel) 3, 1711–1728 (2010).

Article CAS Google Scholar

Pearson, W. B. A Handbook of Lattice Spacings and Structures of Metals and Alloys: International Series of Monographs on Metal Physics and Physical Metallurgy Vol. 4 (Elsevier, 2013).

Google Scholar

Boldman, W. L. et al. Exploring the composition, phase separation and structure of AgFe alloys for magneto-optical applications. Mater. Sci. Eng., B 266, 115044 (2021).

Article CAS Google Scholar

Garfinkel, D. A. et al. Optical and magnetic properties of Ag–Ni bimetallic nanoparticles assembled via pulsed laser-induced dewetting. ACS Omega 5, 19285–19292 (2020).

Article CAS Google Scholar

George, E. P., Raabe, D. & Ritchie, R. O. High-entropy alloys. Nat. Rev. Mater. 4, 515–534 (2019).

Article ADS CAS Google Scholar

Musicó, B. L. et al. The emergent field of high entropy oxides: Design, prospects, challenges, and opportunities for tailoring material properties. APL Mater. 8, 040912 (2020).

Article ADS Google Scholar

Yang, X. & Zhang, Y. Prediction of high-entropy stabilized solid-solution in multi-component alloys. Mater. Chem. Phys. 132, 233–238 (2012).

Article CAS Google Scholar

Xie, P. et al. Highly efficient decomposition of ammonia using high-entropy alloy catalysts. Nat. Commun. 10, 4011 (2019).

Article ADS Google Scholar

Musicó, B. et al. Tunable magnetic ordering through cation selection in entropic spinel oxides. Phys. Rev. Mater. 3, 104416 (2019).

Article Google Scholar

Tang, N. et al. Magnetism in metastable and annealed compositionally complex alloys. Phys. Rev. Mater. 5, 114405 (2021).

Article CAS Google Scholar

Chaturvedi, U. C., Shrivastava, R. & Upreti, R. K. Viral infections and trace elements: A complex interaction. Curr. Sci. 87, 1536–1554 (2004).

CAS Google Scholar

Li, Z. et al. Cu-bearing high-entropy alloys with excellent antiviral properties. J. Mater. Sci. Technol. 84, 59–64 (2021).

Article ADS CAS Google Scholar

Liu, Y. et al. Combinatorial development of antibacterial Zr-Cu-Al-Ag thin film metallic glasses. Sci. Rep. 6, 26950 (2016).

Article ADS CAS Google Scholar

Etiemble, A. et al. Innovative Zr-Cu-Ag thin film metallic glass deposed by magnetron PVD sputtering for antibacterial applications. J. Alloy. Compd. 707, 155–161 (2017).

Article CAS Google Scholar

Jabed, A. et al. Property optimization of Zr-Ti-X (X = Ag, Al) metallic glass via combinatorial development aimed at prospective biomedical application. Surf. Coat. Technol. 372, 278–287 (2019).

Article CAS Google Scholar

Hulo, C. et al. ViralZone: a knowledge resource to understand virus diversity. Nucleic Acids Res. 39(suppl_1), D576–D582 (2011).

Article CAS Google Scholar

Tung-Thompson, G., Libera, D. A., Koch, K. L., De Los Reyes, F. L. & Jaykus, L. A. Aerosolization of a human norovirus surrogate, bacteriophage MS2, during simulated vomiting. PLoS ONE 10, e0134277 (2015).

Article Google Scholar

Laktionova, M. A., Tabchnikova, E. D., Tang, Z. & Liaw, P. K. Mechanical properties of the high-entropy alloy Ag0.5CoCrCuFeNi at temperatures of 4.2–300 K. Low Temp. Phys. 39, 630–632 (2013).

Article ADS CAS Google Scholar

Guo, S. S. & Tsai, C. J. Reaction sequence of Co/Ni/Si(001) system. J. Vac. Sci. Technol. A 21, 628–633 (2003).

Article CAS Google Scholar

Song, O., Kim, D., Yoon, C. S. & Kim, C. K. Formation of NiCoSix silicide by thermal annealing of Ni/Co bilayer on Si substrate. Mater. Sci. Semicond. Process. 8, 608–612 (2005).

Article CAS Google Scholar

Wang, L. J. et al. Effects of silver segregation on sputter deposited antibacterial silver-containing diamond-like carbon films. Thin Solid Films 650, 58–64 (2018).

Article ADS CAS Google Scholar

Hargreaves, M. Modulated structures in some copper–nickel–iron alloys. Acta Crystallogr. A 4, 301–309 (1951).

Article CAS Google Scholar

Franciosi, A., Weaver, J. H. & Schmidt, F. A. Electronic structure of nickel silicides ${\mathrm{Ni}}_{2}$Si, NiSi, and Ni${\mathrm{Si}}_{2}$. Phys. Rev. B 26, 546–553 (1982).

Article ADS CAS Google Scholar

Pal, S., Tak, Y. K. & Song, J. M. Does the antibacterial activity of silver nanoparticles depend on the shape of the nanoparticle? A study of the Gram-negative bacterium Escherichia coli. Appl. Environ. Microbiol. 73, 1712–1720 (2007).

Article ADS CAS Google Scholar

Haldar, J., Weight, A. K. & Klibanov, A. M. Preparation, application and testing of permanent antibacterial and antiviral coatings. Nat. Protoc. 2, 2412–2417 (2007).

Article CAS Google Scholar

Nakajo, K. et al. Inhibitory effect of Ti-Ag alloy on artificial biofilm formation. Dent. Mater. J. 33, 389–393 (2014).

Article CAS Google Scholar

Choudhary, S. et al. Oxidation mechanism of thin Cu films: A gateway towards the formation of single oxide phase. AIP Adv. 8, 055114 (2018).

Article ADS Google Scholar

Lass, E. A., Stoudt, M. R. & Campbell, C. E. Systems design approach to low-cost coinage materials. Integr. Mater. Manuf. Innov. 7, 52–69 (2018).

Article Google Scholar

Rakowska, P. D. et al. Antiviral surfaces and coatings and their mechanisms of action. Commun. Mater. 2, 53 (2021).

Article CAS Google Scholar

Lou, Y. et al. Microbiologically influenced corrosion of FeCoCrNiMo0.1 high-entropy alloys by marine Pseudomonas aeruginosa. Corros. Sci. 165, 108390 (2020).

Article CAS Google Scholar

Villapún, V. M., Dover, L. G., Cross, A. & González, S. Antibacterial metallic touch surfaces. Materials (Basel) 9, 736 (2016).

Article ADS Google Scholar

Silhavy, T. J., Kahne, D. & Walker, S. The bacterial cell envelope. Cold Spring Harb. Perspect. Biol. 2, a000414–a000414 (2010).

Article Google Scholar

Cochran, A. L. Impacts of COVID-19 on access to transportation for people with disabilities. Transp. Res. Interdiscip. Perspect. 8, 100263 (2020).

Google Scholar

Download references

This research was supported by the Science Alliance at the University of Tennessee, Knoxville, thorough the JDRD Collaborative Cohort Program Fellowship. Antimicrobial testing was partly supported by NSF award 2028542.

Department of Food Science, University of Tennessee, Knoxville, TN, 37996, USA

Anne F. Murray, Daniel Bryan & Thomas G. Denes

Department of Ecology and Evolutionary Biology, University of Tennessee, Knoxville, TN, 37996, USA

Anne F. Murray

Department of Materials Science and Engineering, University of Tennessee, Knoxville, TN, 37996, USA

David A. Garfinkel, Cameron S. Jorgensen, Nan Tang, WLNC Liyanage, Eric A. Lass, Philip D. Rack & Dustin A. Gilbert

Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN, 37831, USA

Ying Yang

Department of Physics and Astronomy, University of Tennessee, Knoxville, TN, 37996, USA

Dustin A. Gilbert

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

D.A.G., T.D., A.F.M. Y.Y. and P.D.R. conceived and designed the experiments. A.F.M., D.B., and T.D. conducted the microbial experiments. D.A.G. and P.D.R. fabricated the wafers and E.L. fabricated the currency prototype. D.A.G., C.S.J, W.L. and N.T performed the materials characterization. A.F.M., D.A.G., and T.D wrote the manuscript. All authors contributed to the discussion and manuscript revision.

Correspondence to Dustin A. Gilbert.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Murray, A.F., Bryan, D., Garfinkel, D.A. et al. Antimicrobial properties of a multi-component alloy. Sci Rep 12, 21427 (2022). https://doi.org/10.1038/s41598-022-25122-4

Download citation

Received: 30 September 2022

Accepted: 24 November 2022

Published: 11 December 2022

DOI: https://doi.org/10.1038/s41598-022-25122-4

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.